Abstract: A process to form a crosslinked composition comprising thermally treating a composition at a temperature ? 25° C., in the presence of moisture, and wherein the composition comprises the following components: a) an olefin/silane interpolymer, b) a cure catalyst selected from the following: i) a metal alkoxide, ii) a metal carboxylate, iii) a metal sulfonate, iv) an aryl sulfonic acid, v) a tris-aryl borane, vi) any combination of two or more from i)-v). Also, a composition comprising the following components a and b, as described above. A process to form an olefin/alkoxysilane interpolymer, and the corresponding composition, said process comprising thermally treating a composition comprising the following components: a) an olefin/silane interpolymer, b) an alcohol, and c) a Lewis acid.

Abstract: Embodiments of the invention provide a class of butene/?-olefin block interpolymers. The butene/?-olefin inter-polymers are characterized by an average block index, ABI, which is greater than zero and up to about 1.0 and a molecular weight distribution, Mw/Mn, greater than about 1.3. Preferably, the block index is from about 0.2 to about 1. In addition or alternatively, the block butene/?-olefin interpolymer is characterized by having at least one fraction obtained by Temperature Rising Elution Fractionation (‘TREF’), wherein the fraction has a block index greater than about 0.3 and up to about 1.0 and the butene/?-olefin interpolymer has a molecular weight distribution, Mw/Mn, greater than about 1.4.

Abstract: Embodiments of the invention provide a class of ethylene/?-olefin block interpolymers. The ethylene/?-olefin interpolymers are characterized by an average block index, ABI, which is greater than zero and up to about 1.0 and a molecular weight distribution, Mw/Mn, greater than about 1.3. Preferably, the block index is from about 0.2 to about 1. In addition or alternatively, the block ethylene/?-olefin interpolymer is characterized by having at least one fraction obtained by Temperature Rising Elution Fractionation (‘TREF’), wherein the fraction has a block index greater than about 0.3 and up to about 1.0 and the ethylene/?-olefin interpolymer has a molecular weight distribution, Mw/Mn, greater than about 1.4.

Abstract: Bis(salicylaldiminato)titanium complex with optionally substituted phenyl or cyclohexyl on nitrogen catalyzes highly syndiospecific polymerization of propylene. Syndiotactic polypropylene with defects of the type rmr having [rrrr] content greater than 0.70 and block copolymer containing block(s) of the syndiotactic polypropylene and block(s) of poly(ethylene-co-propylene) and/or poly(alpha-olefin-co-propylene) are obtained. Certain of the catalysts provide living polymerization. Living olefin polymers and olefin terminated oligomers and polymers are also products.