Abstract: This invention provides a film or sheet capable of being thermoformed into a shaped article and being formed from a blend of about 60 to 85 parts by weight of a polyethylene terephthalate having an intrinsic viscosity of at least about 0.90, about 15 to 40 parts by weight of a polycarbonate and about 5 to 20 parts by weight of a non-acidic silica filler, such as novaculite, the polyethylene terephthalate portion of the film or sheet having a degree of crystallinity in the range of about 20 to 40%. The present invention also provides compositions for forming such films and sheets and shaped articles thermoformed from such films or sheets, such as cook-in-trays. This invention also provides a process of forming such films or sheets.

Abstract: A polyester sheet containing an antiblock agent is produced by uniformly blending a small amount of a degraded polycarbonate containing the antiblock agent. The antiblock agent must have an inherent or adjusted pH of less than six to degrade the polycarbonate to lower its molecular weight upon extrusion compounding. This in turn makes a uniform blend and resulting clear sheet with antiblocking properties. In another embodiment, larger amounts of polycarbonate containing the antiblock agent are used.

Abstract: This invention provides a film or sheet capable of being thermoformed into a shaped article and being formed from a blend of about 60 to 85 parts by weight of a polyethylene terephthalate having an intrinsic viscosity of at least about 0.90, about 15 to 40 parts by weight of a polycarbonate and about 5 to 20 parts by weight of a non-acidic silica filler, such as novaculite, the polyethylene terephthalate portion of the film or sheet having a degree of crystallinity in the range of about 20 to 40%. The present invention also provides compositions for forming such films and sheets and shaped articles thermoformed from such films or sheets, such as cook-in-trays. This invention also provides a process of forming such films or sheets.