Abstract: The present invention relates to a novel process for the anionic polymerization of lactam monomers.

Abstract: The present invention relates to a process for producing polyamides, preferably crosslinked polyamides, via anionic polymerization of lactams in the presence of an anionic catalyst and of a caprolactam-capped polyisocyanate, where said isocyanate comprises more than 3.5 capped isocyanate groups.

Abstract: A heat treatment device for a material in powder form, including a heat treatment furnace including a heating zone and a quenching tank. The quenching tank includes a container at least partially filled with a plurality of precooled solid elements, and the heat treatment furnace is mounted in a mobile manner to allow the content of the heat treatment furnace to be transferred to the quenching tank. A corresponding heat treatment method, for example, can implement manufacture of lamellar lithium manganese nickel magnesium oxide.

Abstract: Semiaromatic, semicrystalline copolyamide molding compositions, comprising A) from 35 to 100% by weight of a copolyamide composed of a1) from 35 to 69% by weight of units which derive from hexamethylenediamine and from an aromatic dicarboxylic acid having from 8 to 16 carbon atoms, a2) from 31 to 65% by weight of units which derive from 3,3?-dimethyl-4,4?-diaminodicyclohexylmethane and from terephthalic acid, a3) from 0 to 30% by weight of units of a semicrystalline polyamide different from a1) and a2), B) from 0 to 65% by weight of further additives, where the total of the percentages by weight of A) and B) is 100%.

Abstract: A lactam composition which comprises the following components: from 3 to 25% by weight of a random vinylaromatic-diene copolymer (A), where the random vinylaromatic-diene copolymer is composed of at least one block (S) which forms a hard phase and which is composed of vinylaromatic monomers, and of at least one random block (S/B) which forms a soft phase and which has vinylaromatic monomers and diene monomers, from 75 to 97% by weight of at least one lactam component (B), and also optionally reinforcing materials and/or additives has improved viscosity in the melt and can be used for producing polyamide moldings.

Abstract: The present invention relates to a process for producing moldings comprising (A) at least one lactam, (B) at least one activator, and (C) at least one catalyst, where (A) to (C) proceed through treatments comprising a) mixing of (A), (B), and (C), b) metering of (A), (B), and (C) into an apparatus for producing mixture droplets, and producing mixture droplets, and c) depositing the mixture droplets comprising (A), (B), and (C) on a belt, and d) producing moldings.

Abstract: The present invention relates to polyamide moldings obtainable via anionic polymerization of a lactam comprising microcapsules with a capsule core made of latent-heat-accumulator material and a polymer as capsule wall, to a process for producing the same, and also to the use of the same in motor-vehicle construction, as battery housing, as housing for small electronic devices, and for heat-retention systems for foods.

Abstract: The invention relates to a process for preparing polymers from monomers and/or oligomers by adding a liquid comprising the monomers and/or oligomers dropwise to a continuous liquid phase in a reactor, the continuous liquid phase being immiscible with the liquid comprising the monomers and/or oligomers, and the monomers and/or oligomers reacting in the continuous liquid phase to give the polymer. The liquid comprising the monomers and/or oligomers is shaped to droplets outside the continuous liquid phase, which are subsequently introduced into the continuous liquid phase. The invention further relates to a reactor for performing the process, comprising a tube through which a continuous liquid phase flows, and means of generating droplets, the means of generating droplets being arranged such that the droplets are generated outside the continuous liquid phase and then introduced into the continuous liquid phase.

Abstract: The invention relates to a process for preparing polymers from monomers and/or oligomers by adding a liquid comprising the monomers and/or oligomers dropwise to a continuous liquid phase in a reactor, the continuous liquid phase being immiscible with the liquid comprising the monomers and/or oligomers, and the monomers and/or oligomers reacting in the continuous liquid phase to give the polymer. The liquid comprising the monomers and/or oligomers is shaped to droplets outside the continuous liquid phase, which are subsequently introduced into the continuous liquid phase. The invention further relates to a reactor for performing the process, comprising a tube through which a continuous liquid phase flows, and means of generating droplets, the means of generating droplets being arranged such that the droplets are generated outside the continuous liquid phase and then introduced into the continuous liquid phase.

Abstract: The present invention relates to polyamide composites containing graphene, a method for producing them and to their use as or for producing a material with gas barrier and/or electroconductive and/or thermally conductive properties and/or a mechanically reinforced material.

Abstract: The use of thermoplastic molding materials comprising A) 10 to 98.8% by weight of a mixture formed from a1) 40 to 70% by weight of nylon-6,6 or nylon-4,6 or nylon-6 or mixtures thereof, a2) 30 to 60% by weight of a polyamide having a ratio of methylene to amide groups of 7 to 12, B) 1 to 50% by weight of a fibrous or particulate filler, C) 0.1 to 3% by weight of a lubricant, D) 0.05 to 3% by weight of a heat stabilizer, E) 0 to 40% by weight of further additives, where the sum of the percentages by weight A) to E) and a1) and a2) adds to 100%, for production of stress cracking- and corrosion-resistant moldings.

Abstract: In a process for preparing a polyamide based on dicarboxylic acids and diamines in an extruder, a solid mixture comprising a monomer mixture composed of 50 mol % of dicarboxylic acid mixture composed of from 60 to 88 % by weight of terephthalic acid and from 12 to 40% by weight of isophthalic acid, in which up to 20% by weight of the dicarboxylic acid mixture may also be replaced by other dicarboxylic acids, and 50 mol % of hexamethylenediamine which may be up to 20% by weight replaced by other C2-30-diamines, in a corotatory twin-screw extruder for a residence time of from 10 seconds to 30 minutes, is heated to a temperature in the range from 150 to 400° C. while removing steam and if appropriate diamines through venting orifices.

Abstract: The process for preparing a polyamide based on dicarboxylic acids and diamines has the following stages: 1) providing an aqueous monomer mixture of dicarboxylic acids and diamines, the molar ratio of dicarboxylic acids to diamines being adjusted such that a molar deficiency of dicarboxylic acids or diamines of from 1 to 10 mol % is present at the outlet of stage 3), based on the other component in each case, 2) transferring the aqueous mixture from stage 1) to a continuous evaporator reactor in which diamines and dicarboxylic acids are reacted at a temperature in the range from 100 to 370° C. and a pressure in the range from 1 to 50 bar, 3) transferring the mixture from stage 2) to a separator which is operated at a temperature in the range from 100 to 370° C.

Abstract: The present invention relates to a process for the production of a fiber-reinforced composite material with a polyamide matrix.

Abstract: The present invention relates to a novel process for preparing polyisocyanates having isocyanurate groups by a partial trimerization of (cyclo)aliphatic diisocyanates in the presence of at least one trimerization catalyst from the group of ammonium salts of lactames and to the use of the thus obtainable polyisocyanates having isocyanurate groups as a polyisocyanate component in polyurethane coatings.

Abstract: The present invention relates to solid particles which comprise at least one lactam, and also at least one activator, and at least one catalyst, to a process for the production of these, and also to the use of these for the production of polyamide, and to a process for the production of polyamide.

Abstract: What are described are a solution comprising a terpolymer formed from the monomers of components A, B and C, the total amount of which adds up to 100% by weight, a) 5 to 60% by weight of lactams as component A, b) 5 to 60% by weight of equimolar amounts of adipic acid and one or more aliphatic diamines as component B, c) 10 to 70% by weight of equimolar amounts of adipic acid and 4,4?-diaminodicyclohexylmethane (dicycan) as component C, in an aromatics-free solvent system comprising 50 to 100% by weight of C1-4-alkanol, 0 to 50% by weight of water and not more than 10% by weight of further aromatics-free solvents, where the total amount of the solvent system adds up to 100% by weight, and a terpolymer formed from the monomers of components A, B and C, the total amount of which adds up to 100% by weight, a) 15 to 40% by weight of lactams as component A, b) 20 to 45% by weight of equimolar amounts of adipic acid and one or more aliphatic diamines as component B, c) 25 to 60% by weight of equimolar amounts of

Abstract: The present invention relates to a novel process for preparing polyisocyanates having isocyanurate groups by a partial trimerization of (cyclo)aliphatic diisocyanates in the presence of at least one trimerization catalyst from the group of ammonium salts of lactames and to the use of the thus obtainable polyisocyanates having isocyanurate groups as a polyisocyanate component in polyurethane coatings.

Abstract: The present invention relates to a process for producing polyamide moldings by subjecting a lactam-containing polymerizable composition to a rotomolding process.

Abstract: Thermoplastic molding compositions, comprising A) from 10 to 99.999% by weight of a polyimide B) from 0.001 to 20% by weight of iron powder with a particle size of at most 10 ?m (d50 value), which is obtainable via thermal decomposition of pentacarbonyliron, C) from 0 to 70% by weight of further additives, where the total of the percentages by weight of components A) to C) is 100%.