Abstract: Single crystal CVD diamond material comprising a total nitrogen concentration of at least 5 ppm and a neutral single substitutional nitrogen, Ns0, to total single substitutional nitrogen, Ns, ratio of at least 0.7. Such a diamond is observed to have a relatively low amount of brown colouration despite the relatively high concentration of nitrogen. A method of making the single crystal diamond is also disclosed, the method including growing the CVD diamond in process gases comprising 60 to 200 ppm nitrogen, in addition to a carbon-containing gas, and hydrogen, wherein the ratio of carbon atoms in the carbon-containing gas to hydrogen atoms in the hydrogen gas is 0.5 to 1.5%.

Abstract: Single crystal CVD diamond material comprising a total nitrogen concentration of at least 5 ppm and a neutral single substitutional nitrogen. Ns0, to total single substitutional nitrogen, Ns, ratio of at least 0.7. Such a diamond is observed to have a relatively low amount of brown colouration despite the relatively high concentration of nitrogen A method of making the single crystal diamond is also disclosed, the method including growing the CVD diamond in process gases comprising 60 to 200 ppm nitrogen, in addition to a carbon-containing gas, and hydrogen, wherein the ratio of carbon atoms in the carbon-containing gas to hydrogen atoms in the hydrogen gas is 0.5 to 1.5%.

Abstract: A method of forming a diamond composite body and the diamond composite body. A first single crystal diamond body is provided, which contains nitrogen and has a uniform strain such that over an area of at least 1×1 mm, at least 90 percent of points display a modulus of strain-induced shift of NV resonance of less than 200 kHz, wherein each point in the area is a resolved region of 50 ?m2. The first single crystal diamond body is treated to convert at least some of the nitrogen to form at least 0.3 ppm nitrogen-vacancy, NV?, centres. A CVD process is used to grow a second single crystal diamond body on a surface of the first single crystal diamond body. The second single crystal diamond body has an NV concentration less than or equal to 10 times lower than the NV? concentration in the first single crystal diamond body.

Abstract: Single crystal CVD diamond material comprising a total nitrogen concentration of at least 5 ppm and a neutral single substitutional nitrogen. Ns0, to total single substitutional nitrogen, Ns, ratio of at least 0.7. Such a diamond is observed to have a relatively low amount of brown colouration despite the relatively high concentration of nitrogen A method of making the single crystal diamond is also disclosed, the method including growing the CVD diamond in process gases comprising 60 to 200 ppm nitrogen, in addition to a carbon-containing gas, and hydrogen, wherein the ratio of carbon atoms in the carbon-containing gas to hydrogen atoms in the hydrogen gas is 0.5 to 1.5%.