Abstract: A high strength and toughness seamless steel tube for an automobile airbag, comprising the following elements, by wt %: C: 0.05-0.15%; Si: 0.1-0.45%; Mn: 1.0-1.9%; Ni: 0.1-0.6%; Cr: 0.05-1.0%; Mo: 0.05-0.2%; Cu: 0.05-0.50%; Al: 0.015-0.060%; Nb: 0.02-0.1%; V: 0.02-0.15%; and the balance being Fe and other inevitable impurities. A method for manufacturing the seamless steel tube comprises the steps: (1) heating a tube blank and then soaking; (2) hot piercing, reducing the diameter and the wall thickness of the tube blank with a stretch reducer and then cooling naturally; (3) annealing, pickling, phosphating and saponifying; (4) cold working to obtain a finished product size; and (5) carrying out stress relief annealing treatment.

Abstract: A high strength and toughness seamless steel tube for an automobile airbag, comprising the following elements, by wt %: C: 0.05-0.15%; Si: 0.1-0.45%; Mn: 1.0-1.9%; Ni: 0.1-0.6%; Cr: 0.05-1.0%; Mo: 0.05-0.2%; Cu: 0.05-0.50%; Al: 0.015-0.060%; Nb: 0.02-0.1%; V: 0.02-0.15%; and the balance being Fe and other inevitable impurities. A method for manufacturing the seamless steel tube comprises the steps: (1) heating a tube blank and then soaking; (2) hot piercing, reducing the diameter and the wall thickness of the tube blank with a stretch reducer and then cooling naturally; (3) annealing, pickling, phosphating and saponifying; (4) cold working to obtain a finished product size; and (5) carrying out stress relief annealing treatment.

Abstract: A 500 MPa grade longitudinally welded steel pipe with a low yield ratio and a manufacturing method therefor, the components thereof by weight percentages being as follows: C 0.11%-0.16%, Si 0.15%-0.35%, Mn 0.8%-1.5%, V 0.06%-0.15%, Al 0.002%-0.04%, Ti 0%-0.05%, Nb 0%-0.05%, the balance being Fe and inevitable impurities, and the carbon equivalent Ceq being not more than 0.4%. According to the above component design, molten steel is subjected to smelting in a converter or electric furnace, and is cast into a slab; the slab is heated at 1,200° C.-1,300° C. and rolled into a plate strip, with the finished rolling temperature of the plate strip being between 840° C.-940° C.; the rolled plate strip is subjected to laminar flow cooling with a water curtain, the laminar flow cooling adopting the manner of rear-section cooling, and is coiled into a plate roll when being cooled to the temperature interval of 500° C.-560° C.

Abstract: A 500 MPa grade longitudinally welded steel pipe with a low yield ratio and a manufacturing method therefor, the components thereof by weight percentages being as follows: C 0.11%-0.16%, Si 0.15%-0.35%, Mn 0.8%-1.5%, V 0.06%-0.15%, Al 0.002%-0.04%, Ti 0%-0.05%, Nb 0%-0.05%, the balance being Fe and inevitable impurities, and the carbon equivalent Ceq being not more than 0.4%. According to the above component design, molten steel is subjected to smelting in a converter or electric furnace, and is cast into a slab; the slab is heated at 1,200° C.-1,300° C. and rolled into a plate strip, with the finished rolling temperature of the plate strip being between 840° C.-940° C.; the rolled plate strip is subjected to laminar flow cooling with a water curtain, the laminar flow cooling adopting the manner of rear-section cooling, and is coiled into a plate roll when being cooled to the temperature interval of 500° C.-560° C.