Abstract: The present disclosure provides a wire material cleaning device, method, and use. The present disclosure provides a wire material cleaning device, including a charged dust collecting unit, wherein the charged dust collecting unit comprises a corona wire and a tubular dust-collecting anode plate, and the corona wire is located at a center position in an axial direction of the tubular dust-collecting anode plate.

Abstract: The present disclosure provides an intermediate alloy and a preparation method therefor, and use thereof. The preparation method of the intermediate alloy includes the following steps: S1, performing stranding by taking a wire material of a doping element as a core material and taking a base material wire as a peripheral stranding wire to obtain a first stranding wire; S2, performing diffusion welding on the first stranding wire in a vacuum environment or under a protection of an inert atmosphere, so that a metallurgical bonding is formed between the wire material of the doping element and the base material wire, so as to obtain a second stranding wire; and S3, drawing the second stranding wire to obtain an intermediate alloy wire.

Abstract: The present disclosure provides an intermediate alloy and a preparation method therefor, and use thereof. The preparation method of the intermediate alloy includes the following steps: S1, performing stranding by taking a wire material of a doping element as a core material and taking a base material wire as a peripheral stranding wire to obtain a first stranding wire; S2, performing diffusion welding on the first stranding wire in a vacuum environment or under a protection of an inert atmosphere, so that a metallurgical bonding is formed between the wire material of the doping element and the base material wire, so as to obtain a second stranding wire; and S3, drawing the second stranding wire to obtain an intermediate alloy wire.

Abstract: The present disclosure relates to a copper-phosphorus-zinc-tin brazing sheet and a preparation method and use thereof. The copper-phosphorus-zinc-tin brazing sheet includes a copper core layer, CuP alloy layers respectively arranged on two sides of the copper core layer, and at least two SnZn alloy layers respectively arranged on the other sides of the two CuP alloy layers away from the copper core layer.

Abstract: A copper-tin brazing wire and a preparation method and use thereof are provided. A copper-tin brazing wire includes a plurality of copper wires each having a composite metal layer on a surface thereof; the copper-tin brazing wire includes, in parts by weight, 75-84 parts of Cu, 20-25 parts of Sn, and 0.4-0.5 parts of P; and the composite metal layer includes Cu, Sn, and P, in which a mass ratio of Cu, Sn, and P is (45-55):(46-56):(0.5-1.5).

Abstract: The present disclosure relates to the field of brazing material technologies, and particularly to a copper-phosphorus brazing wire for brazing a copper alloy spectacle frame as well as a preparing method and system thereof. The copper-phosphorus brazing wire for brazing a copper alloy spectacle frame includes components with following mass percentage, 87.1%˜91.4% of Cu, 1.5%˜2.6% of Ag, 5.9%˜8.4% of P, 0.2%˜0.42% of Al and 0.8%˜1.68% of Si. For the copper-phosphorus brazing wire according to the present disclosure, through coordination and cooperation of the components, impurity content is low and joint strength is high in a welding process; a mass ratio of the Si to the Al is a constant value, and a dense oxide film may be formed on a surface of a molten pool to hinder volatilization of Zn in a base material.

Abstract: The present disclosure provides a copper-phosphorus-tin brazing wire and a preparation method thereof, relates to the technical field of brazing materials. The copper-phosphorus-tin brazing wire is of a three-layer structure, the inner layer is Cu, the middle layer is Cu-14P alloy, and the outer layer is Sn, wherein the mass percentage of Sn is over 7%. The present disclosure solves the technical problems in the prior art that the copper-phosphorus-silver brazing filler metal is prone to produce defects such as pores and inclusions when brazing copper alloys, which leads to the decline of the mechanical properties of the joint, and simultaneously provides the preparation method of the copper-phosphorus-tin brazing wire, such that the technical problem that it is difficult to obtain copper-phosphorus-tin brazing wire with a wire diameter below 0.5 mm under the condition of high Sn content is solved.

Abstract: The present disclosure relates to a copper-phosphorus-zinc-tin brazing sheet and a preparation method and use thereof. The copper-phosphorus-zinc-tin brazing sheet includes a copper core layer, CuP alloy layers respectively arranged on two sides of the copper core layer, and at least two SnZn alloy layers respectively arranged on the other sides of the two CuP alloy layers away from the copper core layer.

Abstract: The present disclosure provides a copper-phosphorus-tin brazing wire and a preparation method thereof, relates to the technical field of brazing materials. The copper-phosphorus-tin brazing wire is of a three-layer structure, the inner layer is Cu, the middle layer is Cu-14P alloy, and the outer layer is Sn, wherein the mass percentage of Sn is over 7%. The present disclosure solves the technical problems in the prior art that the copper-phosphorus-silver brazing filler metal is prone to produce defects such as pores and inclusions when brazing copper alloys, which leads to the decline of the mechanical properties of the joint, and simultaneously provides the preparation method of the copper-phosphorus-tin brazing wire, such that the technical problem that it is difficult to obtain copper-phosphorus-tin brazing wire with a wire diameter below 0.5 mm under the condition of high Sn content is solved.

Abstract: The present disclosure relates to the field of brazing material technologies, and particularly to a copper-phosphorus brazing wire for brazing a copper alloy spectacle frame as well as a preparing method and system thereof. The copper-phosphorus brazing wire for brazing a copper alloy spectacle frame includes components with following mass percentage, 87.1%˜91.4% of Cu, 1.5%˜2.6% of Ag, 5.9%˜8.4% of P, 0.2%˜0.42% of Al and 0.8%˜1.68% of Si. For the copper-phosphorus brazing wire according to the present disclosure, through coordination and cooperation of the components, impurity content is low and joint strength is high in a welding process; a mass ratio of the Si to the Al is a constant value, and a dense oxide film may be formed on a surface of a molten pool to hinder volatilization of Zn in a base material.

Abstract: A copper-tin brazing wire and a preparation method and use thereof are provided. A copper-tin brazing wire includes a plurality of copper wires each having a composite metal layer on a surface thereof; the copper-tin brazing wire includes, in parts by weight, 75-84 parts of Cu, 20-25 parts of Sn, and 0.4-0.5 parts of P; and the composite metal layer includes Cu, Sn, and P, in which a mass ratio of Cu, Sn, and P is (45-55):(46-56):(0.5-1.5).

Abstract: A brazing material outer coat and a method for preparing the same, an in-situ synthetic metal-coated flux-cored silver brazing material and a method for preparing the same, a welding method and a joint body, wherein the in-situ synthetic metal-coated flux-cored silver brazing material comprises a flux core and a brazing material outer coat wrapping the flux core, the brazing material outer coat comprises, in percentage by weight: silver Ag 20.0˜36.0%, copper Cu 35.0˜45.0%, zinc Zn 27.0˜37.0%, tin Sn 1.0˜3.0%, phosphorus P 0.1%˜0.5%, nickel Ni 0.5˜2.0%, germanium Ge 0.1˜0.3%, and lithium Li 0.1˜0.3%, the flux core comprises, in percentage by weight: elemental boron micropowder 5.0˜10.0%, sodium borohydride 5.0˜10.0%, potassium fluoroborate 15.0˜30.0%, boric anhydride 25.0˜40.0%, sodium fluoride 10.0˜30.0%, sodium bifluoride 2.0˜4.0%, and copper sulfate 1.0˜5.0%.

Abstract: A brazing material outer coat and a method for preparing the same, an in-situ synthetic metal-coated flux-cored silver brazing material and a method for preparing the same, a welding method and a joint body, wherein the in-situ synthetic metal-coated flux-cored silver brazing material comprises a flux core and a brazing material outer coat wrapping the flux core, the brazing material outer coat comprises, in percentage by weight: silver Ag 20.0˜36.0%, copper Cu 35.0˜45.0%, zinc Zn 27.0˜37.0%, tin Sn 1.0˜3.0%, phosphorus P 0.1%˜0.5%, nickel Ni 0.5˜2.0%, germanium Ge 0.1˜0.3%, and lithium Li 0.1˜0.3%, the flux core comprises, in percentage by weight: elemental boron micropowder 5.0˜10.0%, sodium borohydride 5.0˜10.0%, potassium fluoroborate 15.0˜30.0%, boric anhydride 25.0˜40.0%, sodium fluoride 10.0˜30.0%, sodium bifluoride 2.0˜4.0%, and copper sulfate 1.0˜5.0%.