Abstract: The invention relates to compositions containing transparent thermoplastic polymers and surface modified oxide particles having a particle size of less than 200 nm. The invention also relates to the production and use thereof, in addition to items produced from said compositions.

Abstract: Nanoscale corundum powders are obtained by first producing an Al2O3 precursor by adding seed crystals to an aqueous solution of an aluminium compound and adding a base and then converting the Al2O3 precursor into corundum by calcination at a high temperature. Before the calcination, the salts that are present in addition to the Al2O3 precursor are separated off. The resulting product is calcined at temperatures of 700 to 975° C. and any fines that may be present are removed. The resulting corundum powders can be sintered at temperatures of ≦1200° C. to produce compacts or components of multiple layer systems.

Abstract: The present invention provides compositions containing transparent thermoplastic polymer, surface-modified oxide particles with a particle size of less than 200 nm, and organic NIR absorbers. The compositions of the present invention may find use in reducing diathermancy in sheets, films, glazing systems and roofing systems which may be incorporated into automobiles and buildings.

Abstract: Suspensions and powders based on indium tin oxide are prepared by a method in which indium tin oxide precursors are precipitated from solutions in one or more solvents in the presence of one or more surface-modifying components, the solvent(s) are removed from the precipitate, which is then calcined, one or more surface-modifying components and one or more solvents are added, the mixture is comminuted or dispersed to form a suspension, and the liquid components are separated from the suspension to give a powder. The powder may be converted into a moulding by a shaping process. The materials prepared by this method are especially suitable as coating materials for use in microelectronics and optoelectronics.