Abstract: Polyester materials, methods for making polyesters materials, and uses of the polyester materials in binder materials and articles of manufacture are disclosed. In one embodiment, a process is provided for preparing a polyester solution, including mixing monomers of at least one organic acid containing at least three carboxylic groups and at least one multi-hydroxyl alcohol containing at least three hydroxyl groups to form a reaction mixture, heating the reaction mixture to a first temperature, polymerizing the monomers at the first temperature until reaching an acid value from about 200 to about 400 mg KOH/g, adjusting the temperature to a second temperature less than the first temperature, and forming the polyester solution. The polyester materials may be mixed with cross-linking materials to form binder materials. The binder material may then be used to form articles of manufacture.

Abstract: Compositions and methods for forming condensates and resin compositions are provided. In one embodiment, a condensate is formed from a reaction mixture including a triazine monomer, an arylhydroxy monomer, an aldehyde monomer and an acid catalyst having a pKa value of greater than 3.8. The condensates contain up to 28 wt. % of nitrogen and have a melt viscosity of 3,000 cps or less at 175° C. The condensates may have a solubility of at least 80 wt. % solids dissolved in an organic solvent for 120 hours or greater. Also disclosed are methods for the manufacture of the condensate as well as the condensate's use in fire-retardant epoxy resin compositions suitable for the manufacture of laminates for electronic applications. There is also disclosed a glycidylated triazine-arylhydroxy-aldehyde condensate of this invention.

Abstract: Polyester materials, methods for making polyesters materials, and uses of the polyester materials in binder materials and articles of manufacture are disclosed. In one embodiment, a process is provided for preparing a polyester solution, including mixing monomers of at least one organic acid containing at least three carboxylic groups and at least one multi-hydroxyl alcohol containing at least three hydroxyl groups to form a reaction mixture, heating the reaction mixture to a first temperature, polymerizing the monomers at the first temperature until reaching an acid value from about 200 to about 400 mg KOH/g, adjusting the temperature to a second temperature less than the first temperature, and forming the polyester solution. The polyester materials may be mixed with cross-linking materials to form binder materials. The binder material may then be used to form articles of manufacture.

Abstract: Polyester materials, methods for making polyesters materials, and uses of the polyester materials in binder materials and articles of manufacture are disclosed. In one embodiment, a process is provided for preparing a polyester solution, including mixing monomers of at least one organic acid containing at least three carboxylic groups and at least one multi-hydroxyl alcohol containing at least three hydroxyl groups to form a reaction mixture, heating the reaction mixture to a first temperature, polymerizing the monomers at the first temperature until reaching an acid value from about 200 to about 400 mg KOH/g, adjusting the temperature to a second temperature less than the first temperature, and forming the polyester solution. The polyester materials may be mixed with cross-linking materials to form binder materials. The binder material may then be used to form articles of manufacture.

Abstract: Polyester materials, methods for making polyesters materials, and uses of the polyester materials in binder materials and articles of manufacture are disclosed. In one embodiment, a process is provided for preparing a polyester solution, including mixing monomers of at least one organic acid containing at least three carboxylic groups and at least one multi-hydroxyl alcohol containing at least three hydroxyl groups to form a reaction mixture, heating the reaction mixture to a first temperature, polymerizing the monomers at the first temperature until reaching an acid value from about 200 to about 400 mg KOH/g, adjusting the temperature to a second temperature less than the first temperature, and forming the polyester solution. The polyester materials may be mixed with cross-linking materials to form binder materials. The binder material may then be used to form articles of manufacture.

Abstract: Polyester materials, methods for making polyesters materials, and uses of the polyester materials in binder materials and articles of manufacture are disclosed. In one embodiment, a process is provided for preparing a polyester solution, including mixing monomers of at least one organic acid containing at least three carboxylic groups and at least one multi-hydroxyl alcohol containing at least three hydroxyl groups to form a reaction mixture, heating the reaction mixture to a first temperature, polymerizing the monomers at the first temperature until reaching an acid value from about 200 to about 400 mg KOH/g, adjusting the temperature to a second temperature less than the first temperature, and forming the polyester solution. The polyester materials may be mixed with cross-linking materials to form binder materials. The binder material may then be used to form articles of manufacture.

Abstract: Compositions and methods for forming condensates and resin compositions are provided. In one embodiment, a condensate is formed from a reaction mixture including a triazine monomer, an arylhydroxy monomer, an aldehyde monomer and an acid catalyst having a pKa value of greater than 3.8. The condensates contain up to 28 wt. % of nitrogen and have a melt viscosity of 3,000 cps or less at 175° C. The condensates may have a solubility of at least 80 wt. % solids dissolved in an organic solvent for 120 hours or greater. Also disclosed are methods for the manufacture of the condensate as well as the condensate's use in fire-retardant epoxy resin compositions suitable for the manufacture of laminates for electronic applications. There is also disclosed a glycidylated triazine-arylhydroxy-aldehyde condensate of this invention.