Abstract: Disclosed herein are ethylene-based polymers generally characterized by a melt index of less than 1 g/10 min, a density from 0.93 to 0.965 g/cm3, a CY-a parameter at 190° C. of less than 0.2, an average number of short chain branches per 1000 total carbon atoms of the polymer in a molecular weight range of 400,000 to 600,000 g/mol that is greater than that in a molecular weight range of 40,000 to 60,000 g/mol, and an average number of long chain branches per 1000 total carbon atoms of the polymer in a molecular weight range of 400,000 to 600,000 g/mol that is greater than that in a molecular weight range of 4,000,000 to 6,000,000 g/mol.

Abstract: Disclosed herein are ethylene-based polymers generally characterized by a melt index of less than 15 g/10 min, a density from 0.91 to 0.945 g/cm3, a CY-a parameter at 190° C. from 0.2 to 0.6, an average number of long chain branches per 1,000,000 total carbon atoms of the polymer in a molecular weight range of 500,000 to 2,000,000 g/mol of less than 5, and a maximum ratio of ??/3? at an extensional rate of 0.03 sec?1 in a range from 3 to 15. The ethylene polymers have substantially no long chain branching in the high molecular weight fraction of the polymer, but instead have significant long chain branching in the lower molecular weight fraction, such that polymer melt strength and bubble stability are maintained for the fabrication of blown films and other articles of manufacture.

Abstract: Disclosed herein are ethylene-based polymers generally characterized by a melt index of less than 15 g/10 min, a density from 0.91 to 0.945 g/cm3, a CY-a parameter at 190° C. from 0.2 to 0.6, an average number of long chain branches per 1,000,000 total carbon atoms of the polymer in a molecular weight range of 500,000 to 2,000,000 g/mol of less than 5, and a maximum ratio of ??/3? at an extensional rate of 0.03 sec?1 in a range from 3 to 15. The ethylene polymers have substantially no long chain branching in the high molecular weight fraction of the polymer, but instead have significant long chain branching in the lower molecular weight fraction, such that polymer melt strength and bubble stability are maintained for the fabrication of blown films and other articles of manufacture.

Abstract: Disclosed herein are ethylene-based polymers generally characterized by a melt index of less than 15 g/10 min, a density from 0.91 to 0.945 g/cm3, a CY-a parameter at 190° C. from 0.2 to 0.6, an average number of long chain branches per 1,000,000 total carbon atoms of the polymer in a molecular weight range of 500,000 to 2,000,000 g/mol of less than 5, and a maximum ratio of ?E/3? at an extensional rate of 0.03 sec?1 in a range from 3 to 15. The ethylene polymers have substantially no long chain branching in the high molecular weight fraction of the polymer, but instead have significant long chain branching in the lower molecular weight fraction, such that polymer melt strength and bubble stability are maintained for the fabrication of blown films and other articles of manufacture.

Abstract: Disclosed herein are ethylene-based polymers generally characterized by a melt index of less than 1 g/10 min, a density from 0.93 to 0.965 g/cm3, a CY-a parameter at 190° C. of less than 0.2, an average number of short chain branches per 1000 total carbon atoms of the polymer in a molecular weight range of 400,000 to 600,000 g/mol that is greater than that in a molecular weight range of 40,000 to 60,000 g/mol, and an average number of long chain branches per 1000 total carbon atoms of the polymer in a molecular weight range of 400,000 to 600,000 g/mol that is greater than that in a molecular weight range of 4,000,000 to 6,000,000 g/mol.

Abstract: Disclosed herein are ethylene-based polymers generally characterized by a melt index of less than 1 g/10 min, a density from 0.93 to 0.965 g/cm3, a CY-a parameter at 190° C. of less than 0.2, an average number of short chain branches per 1000 total carbon atoms of the polymer in a molecular weight range of 400,000 to 600,000 g/mol that is greater than that in a molecular weight range of 40,000 to 60,000 g/mol, and an average number of long chain branches per 1000 total carbon atoms of the polymer in a molecular weight range of 400,000 to 600,000 g/mol that is greater than that in a molecular weight range of 4,000,000 to 6,000,000 g/mol.

Abstract: Disclosed herein are ethylene-based polymers generally characterized by a melt index of less than 15 g/10 min, a density from 0.91 to 0.945 g/cm3, a CY-a parameter at 190° C. from 0.2 to 0.6, an average number of long chain branches per 1,000,000 total carbon atoms of the polymer in a molecular weight range of 500,000 to 2,000,000 g/mol of less than 5, and a maximum ratio of ?E/3? at an extensional rate of 0.03 sec?1 in a range from 3 to 15. The ethylene polymers have substantially no long chain branching in the high molecular weight fraction of the polymer, but instead have significant long chain branching in the lower molecular weight fraction, such that polymer melt strength and bubble stability are maintained for the fabrication of blown films and other articles of manufacture.

Abstract: Disclosed herein are ethylene-based polymers generally characterized by a melt index of less than 15 g/10 min, a density from 0.91 to 0.945 g/cm3, a CY-a parameter at 190° C. from 0.2 to 0.6, an average number of long chain branches per 1,000,000 total carbon atoms of the polymer in a molecular weight range of 500,000 to 2,000,000 g/mol of less than 5, and a maximum ratio of ?E/3? at an extensional rate of 0.03 sec?1 in a range from 3 to 15. The ethylene polymers have substantially no long chain branching in the high molecular weight fraction of the polymer, but instead have significant long chain branching in the lower molecular weight fraction, such that polymer melt strength and bubble stability are maintained for the fabrication of blown films and other articles of manufacture.

Abstract: Disclosed are metallocene compounds, catalyst compositions comprising a metallocene compound, processes for polymerizing olefins, methods for making catalyst compositions, olefin polymers and articles made from olefin polymers. In an aspect, a metallocene compounds contain a fluorenyl ligand and a cyclopentadienyl ligand which are bridged by a linking group, in which the metallocene is characterized by [1] the cyclopentadienyl ligand being substituted with a C2-C18 heterohydrocarbyl group having an oxygen atom positioned 5 atoms distance or less from the cyclopentadienyl ligand and [2] the linking group having a pendant C3-C12 alkenyl group having a terminal C?C double bond. It has been discovered that a catalyst composition comprising a metallocene compound having these features can produce polyethylene having a low melt index in the absence of a second metallocene.

Abstract: Ethylene polymers having a density from 0.908 to 0.925 g/cm3, a melt index from 0.5 to 3 g/10 min, a ratio of Mw/Mn from 2 to 4, a ratio of Mz/Mw from 1.6 to 2.3, a CY-a parameter from 0.45 to 0.6, and an ATREF profile characterized by a single peak at a peak ATREF temperature from 76 to 88° C., and by less than 4.5 wt. % of the polymer eluting above a temperature of 91° C. These ethylene polymers can be used to produce various articles of manufacture, such as blown and cast films with a beneficial combination of high tear resistance and low haze.

Abstract: Disclosed herein are ethylene-based polymers generally characterized by a melt index of less than 15 g/10 min, a density from 0.91 to 0.945 g/cm3, a CY-a parameter at 190° C. from 0.2 to 0.6, an average number of long chain branches per 1,000,000 total carbon atoms of the polymer in a molecular weight range of 500,000 to 2,000,000 g/mol of less than 5, and a maximum ratio of ?E/3? at an extensional rate of 0.03 sec?1 in a range from 3 to 15. The ethylene polymers have substantially no long chain branching in the high molecular weight fraction of the polymer, but instead have significant long chain branching in the lower molecular weight fraction, such that polymer melt strength and bubble stability are maintained for the fabrication of blown films and other articles of manufacture.

Abstract: Disclosed are metallocene compounds, catalyst compositions comprising a metallocene compound, processes for polymerizing olefins, methods for making catalyst compositions, olefin polymers and articles made from olefin polymers. In an aspect, a metallocene compounds contain a fluorenyl ligand and a cyclopentadienyl ligand which are bridged by a linking group, in which the metallocene is characterized by [1] the cyclopentadienyl ligand being substituted with a C2-C18 heterohydrocarbyl group having an oxygen atom positioned 5 atoms distance or less from the cyclopentadienyl ligand and [2] the linking group having a pendant C3-C12 alkenyl group having a terminal C?C double bond. It has been discovered that a catalyst composition comprising a metallocene compound having these features can produce polyethylene having a low melt index in the absence of a second metallocene.

Abstract: Ethylene polymers having a density from 0.908 to 0.925 g/cm3, a melt index from 0.5 to 3 g/10 min, a ratio of Mw/Mn from 2 to 4, a ratio of Mz/Mw from 1.6 to 2.3, a CY-a parameter from 0.45 to 0.6, and an ATREF profile characterized by a single peak at a peak ATREF temperature from 76 to 88° C., and by less than 4.5 wt. % of the polymer eluting above a temperature of 91° C. These ethylene polymers can be used to produce various articles of manufacture, such as blown and cast films with a beneficial combination of high tear resistance and low haze.

Abstract: Ethylene polymers having a density from 0.908 to 0.925 g/cm3, a melt index from 0.5 to 3 g/10 min, a ratio of Mw/Mn from 2 to 4, a ratio of Mz/Mw from 1.6 to 2.3, a CY-a parameter from 0.45 to 0.6, and an ATREF profile characterized by a single peak at a peak ATREF temperature from 76 to 88° C., and by less than 4.5 wt. % of the polymer eluting above a temperature of 91° C. These ethylene polymers can be used to produce various articles of manufacture, such as blown and cast films with a beneficial combination of high tear resistance and low haze.

Abstract: Disclosed herein are ethylene-based polymers generally characterized by a melt index of less than 1 g/10 min, a density from 0.93 to 0.965 g/cm3, a CY-a parameter at 190° C. of less than 0.2, an average number of short chain branches per 1000 total carbon atoms of the polymer in a molecular weight range of 400,000 to 600,000 g/mol that is greater than that in a molecular weight range of 40,000 to 60,000 g/mol, and an average number of long chain branches per 1000 total carbon atoms of the polymer in a molecular weight range of 400,000 to 600,000 g/mol that is greater than that in a molecular weight range of 4,000,000 to 6,000,000 g/mol.

Abstract: Disclosed herein are ethylene-based polymers generally characterized by a melt index of less than 1 g/10 min, a density from 0.93 to 0.965 g/cm3, a CY-a parameter at 190° C. of less than 0.2, an average number of short chain branches per 1000 total carbon atoms of the polymer in a molecular weight range of 400,000 to 600,000 g/mol that is greater than that in a molecular weight range of 40,000 to 60,000 g/mol, and an average number of long chain branches per 1000 total carbon atoms of the polymer in a molecular weight range of 400,000 to 600,000 g/mol that is greater than that in a molecular weight range of 4,000,000 to 6,000,000 g/mol.

Abstract: Ethylene polymers having a density from 0.908 to 0.925 g/cm3, a melt index from 0.5 to 3 g/10 min, a ratio of Mw/Mn from 2 to 4, a ratio of Mz/Mw from 1.6 to 2.3, a CY-a parameter from 0.45 to 0.6, and an ATREF profile characterized by a single peak at a peak ATREF temperature from 76 to 88° C., and by less than 4.5 wt. % of the polymer eluting above a temperature of 91° C. These ethylene polymers can be used to produce various articles of manufacture, such as blown and cast films with a beneficial combination of high tear resistance and low haze.

Abstract: Disclosed herein are ethylene-based polymers generally characterized by a melt index of less than 1 g/10 min, a density from 0.93 to 0.965 g/cm3, a CY-a parameter at 190° C. of less than 0.2, an average number of short chain branches per 1000 total carbon atoms of the polymer in a molecular weight range of 400,000 to 600,000 g/mol that is greater than that in a molecular weight range of 40,000 to 60,000 g/mol, and an average number of long chain branches per 1000 total carbon atoms of the polymer in a molecular weight range of 400,000 to 600,000 g/mol that is greater than that in a molecular weight range of 4,000,000 to 6,000,000 g/mol.

Abstract: Disclosed herein are ethylene-based polymers generally characterized by a density from 0.89 to 0.93 g/cm3, a ratio of Mw/Mn from 3 to 6.5, a Mz from 200,000 to 650,000 g/mol, a CY-a parameter at 190° C. from 0.2 to 0.4, and a reverse short chain branching distribution. The ATREF profile of these polymers can have a high temperature peak from 92 to 102° C., and a low temperature peak from 18 to 36° C. less than that of the high temperature peak. These polymers can have comparable physical properties to that of a metallocene-catalyzed LLDPE, but with improved processability, shear thinning, and melt strength, and can be used in blown film and other end-use applications.

Abstract: Disclosed herein are ethylene-based polymers generally characterized by a density from 0.89 to 0.93 g/cm3, a ratio of Mw/Mn from 3 to 6.5, a Mz from 200,000 to 650,000 g/mol, a CY-a parameter at 190° C. from 0.2 to 0.4, and a reverse short chain branching distribution. The ATREF profile of these polymers can have a high temperature peak from 92 to 102° C., and a low temperature peak from 18 to 36° C. less than that of the high temperature peak. These polymers can have comparable physical properties to that of a metallocene-catalyzed LLDPE, but with improved processability, shear thinning, and melt strength, and can be used in blown film and other end-use applications.