Abstract: LEDs employing a III-Nitride light emitting active region deposited on a base layer above a substrate show improved optical properties with the base layer grown on an intentionally misaligned substrate with a thickness greater than 3.5 &mgr;m. Improved brightness, improved quantum efficiency, and a reduction in the current at which maximum quantum efficiency occurs are among the improved optical properties resulting from use of a misaligned substrate and a thick base layer. Illustrative examples are given of misalignment angles in the range from 0.05° to 0.50°, and base layers in the range from 6.5 to 9.5 &mgr;m although larger values of both misalignment angle and base layer thickness can be used. In some cases, the use of thicker base layers provides sufficient structural support to allow the substrate to be removed from the device entirely.

Abstract: LEDs employing a III-Nitride light emitting active region deposited on a base layer above a substrate show improved optical properties with the base layer grown on an intentionally misaligned substrate with a thickness greater than 3.5 &mgr;m. Improved brightness, improved quantum efficiency, and a reduction in the current at which maximum quantum efficiency occurs are among the improved optical properties resulting from use of a misaligned substrate and a thick base layer. Illustrative examples are given of misalignment angles in the range from 0.05° to 0.50°, and base layers in the range from 6.5 to 9.5 &mgr;m although larger values of both misalignment angle and base layer thickness can be used. In some cases, the use of thicker base layers provides sufficient structural support to allow the substrate to be removed from the device entirely.

Abstract: A light emitting device includes several LEDs, mounted on a shared submount, and coupled to circuitry formed on the submount. The LEDs can be of the III-Nitride type. The architecture of the LEDs can be either inverted, or non-inverted. Inverted LEDs offer improved light generation. The LEDs may emit light of the same wavelength or different wavelengths. The circuitry can couple the LEDs in a combination of series and parallel, and can be switchable between various configurations. Other circuitry can include photosensitive devices for feedback and control of the intensity of the emitted light, or an oscillator, strobing the LEDs.

Abstract: For AlGaAs LEDs the confining layers adjoining the active layer possess the highest Al composition. From failure analysis of non-passivated, WHTOL-aged, AlGaAs LEDs, it was discovered that corrosion occurs the fastest at the exposed surfaces of the high Al-content confining layers. By placing a high-quality native oxide at the exposed surfaces of the high Al-content confining layers which protect from the formation of the ‘poor’ oxide, it is possible for LEDs to retain essentially their same light output after 2,000 hours of WHTOL testing. Further, it is possible to improve carrier confinement, carrier injection, wave guiding, and other properties by increasing the Al-content of different layers.

Abstract: For AlGaAs LEDs the confining layers adjoining the active layer possess the highest Al composition. From failure analysis of non-passivated, WHTOL-aged, AlGaAs LEDs, it was discovered that corrosion occurs the fastest at the exposed surfaces of the high Al-content confining layers. By placing a high-quality native oxide at the exposed surfaces of the high Al-content confining layers which protect from the formation of the `poor` oxide, it is possible for LEDs to retain essentially their same light output after 2,000 hours of WHTOL testing. Further, it is possible to improve carrier confinement, carrier injection, wave guiding, and other properties by increasing the Al-content of different layers.