Abstract: The invention relates to a flame-retardant filler based on aluminium hydroxide, its use in polymers and a method for its production, in which aluminium hydroxide in the form of bayerite or a bayerite/gibbsite mixture is modified under pressure at temperatures of at least 170° C. in the presence of water and crystal growth regulator, the aluminium hydroxide used as starting material having an average particle size d50 from 0.1 to 4 ?m.

Abstract: Aluminum hydroxide particles having improved thermal stability and their use as a flame retardant in resins suitable for use in epoxy laminates, and laminates containing the same.

Abstract: The invention relates to a flame retarding composition that comprises a mixture of a metal hydroxide component and a clay component, the mixture being present in the form of dried particles with monomodal particle size distribution.

Abstract: The invention relates to a cross-linkable, halogen-free, flame-resistant plastic mixture which can especially be used, in a cross-linkable state, for coating cables. The inventive plastic mixture comprises the following plastic components: (a) 3 to 50 weight parts (phr) of at least one ethylene copolymer from the group comprising ethylene vinyl acetates, ethylene ethyl acrylates, ethylene methyl acrylates or ethylene butyl acrylates, (b) 30 to 96 weight parts (phr) of a high-density polyolefin, especially a HDPE (High Density Polyethylene) having a density of >0.94 g/cm3, and (c) 1 to 20 weight parts (phr) of a polyolefin which has been grafted with a derivative of an unsaturated carboxylic acid, especially HDPE-g carboxylic acid derivatives. Components (a) to (c) together produce a total of 100 weight parts (phr) of plastic. The mixture also comprises the following components: (d) 40 to 250 weight parts (phr) of a filling material, and (c) 0.1 to 15 weight parts (phr) of a stabilizer system.

Abstract: Boehmite (alumina monohydrate) when used with a typical epoxy resin advanced with phosphorus makes it possible to improve thermal stability and to increase the ignition time of laminates formed from prepregs made using this fortified resin. Such laminates have exceptionally high thermal stability and showed similar longer times to ignition as compared to corresponding resins in which alumina trihydrate was used.

Abstract: Disclosed is a method for producing surface-modified fillers by spray-drying an aqueous suspension of a filler that consists of fine particles, whereby 0.1 to 50 wt. % (calculated as dry substance), preferably 0.3 up to less than 1 wt %, of an aqueous dispersion of a thermoplastic polymer or copolymer or a caoutchouc are added. Said fillers have improved bulk material stability and improved pourability. The inventive fillers are particularly suitable as flame-retardant fillers for synthetic materials or rubber, in a cable insulation for instance.

Abstract: The invention relates to a novel polypropylene compound based on halogen-free, flame-resistant filling materials containing magnesium hydroxide, said compound having good extrudability and improved flame protective action.

Abstract: There are described surface-coated magnesium hydroxides with a coating of

Abstract: A cost-favourable process for the preparation of filled halogen-free self-extinguishing polymer compounds (HFFR compounds) based on halogen-free flame-retardant aluminium- or magnesium-hydroxide-containing fillers by an in-situ filler modification is described.

Abstract: The invention relates to a cross linkable, halogen-free, flame-resistant plastic mixture which can especially be used, in a cross linkable state, for coating cables. The inventive plastic mixture comprises the following plastic components: (a) 3 to 50 weight parts (phr) of at least one ethylene copolymer from the group comprising ethylene vinyl acetates, ethylene ethyl acrylates, ethylene methyl acrylates or ethylene butyl acrylates, (b) 30 to 96 weight parts (phr) of a high-density polyolefin, especially a HDPE (High Density Polyethylene) having a density of >0.94 g/cm3, and (c) 1 to 20 weight parts (phr) of a polyolefin which has been grafted with a derivative of an unsaturated carboxylic acid, especially HPDE-g carboxylic acid derivatives. Components (a) to (c) together produce a total of 100 weight parts (phr) of plastic. The mixture also comprises the following components: (d) 40 to 250 weight parts (phr) of a filling material, and (e) 0.1 to 15 weight parts (phr) of a stabiliser system.

Abstract: Disclosed is a method for producing surface-modified fillers by spray-drying an aqueous suspension of a filler that consists of fine particles, whereby 0.1 to 50 wt. % (calculated as dry substance), preferably 0.3 up to less than 1 wt %, of an aqueous dispersion of a thermoplastic polymer or copolymer or a caoutchouc are added. Said fillers have improved bulk material stability and improved pourability. The inventive fillers are particularly suitable as flame-retardant fillers for synthetic materials or rubber, in a cable insulation for instance.

Abstract: Surface-modified filling material composition for thermoplastic, duroplastic or elastomeric materials, which is a halogen-free, flame-retardant filling material. The filling material is surface-treated with organotitanates and/or with organozirconates and with a siloxane derivative.