Abstract: A method is provided for obtaining uniform grain growth within .gamma.' precipitation strengthened nickel-base superalloys. The method includes forming a billet having a very fine grain size in order to achieve optimum superplasticity of the superalloy during forging. The article is then heated to a pre-working hold temperature in a manner which prevents coarsening of the microstructure and a loss of superplasticity. The article is then worked, such as by forging, at a temperature below the .gamma.' solvus temperature of the alloy, so as to maintain local strain rates within the article below a critical strain rate for random grain growth, and so as to maintain the strain rate gradient throughout the article below a critical upper limit. After working, the article is subjected to annealing at a temperature which is less than the .gamma.' solvus temperature of the alloy, and for a duration which is sufficient to remove accumulated metallurgical strain in the article.