Abstract: Disclosed is a method of producing a surface-treated steel sheet for organic resin coating comprising: applying, to a surface of a zinc or zinc alloy coated or plated steel sheet, a surface-treatment solution containing a resin compound having a specific bisphenol skeleton, a cationic urethane resin emulsion, a silane coupling agent having a specific reactive functional group, an organic titanium chelate compound, a tetravalent vanadium compound, a molybdate compound, a fluorine compound, and water in a specific ratio and with a pH of 4 to 5 to form a surface-treatment layer such that a coating weight of the surface-treatment layer per surface after drying of the surface-treatment solution is 0.005 g/m2 to 1.8 g/m2.

Abstract: Disclosed is a surface-treatment solution for producing a zinc or zinc alloy coated steel sheet with a surface-coating layer that does not contain a chromium compound in the surface-coating layer and that is excellent in all of heat discoloration resistance, heat cracking resistance, planar part anti-corrosion property, corrosion resistance after alkali degreasing, blackening resistance, stack blackening resistance, anti-water stain property, solvent resistance, perspiration resistance, coating adhesion property, and storage stability. The disclosed surface-treatment solution contains a glycidyl group-containing silane coupling agent (A), a tetraalkoxysilane (B), a zirconium carbonate compound (C), and an anionic polyurethane resin (D) having a glass transition temperature (Tg) of 80° C. to 130° C., a vanadium compound (E), a molybdic acid compound (F), and water, the surface-treatment solution having a pH of 8.0 to 10.0, and the amount of each component satisfying a predetermined relationship.

Abstract: Disclosed is a surface-treatment solution for producing a zinc or zinc alloy coated steel sheet with a surface-coating layer that does not contain a chromium compound in the surface-coating layer and that is excellent in all of heat discoloration resistance, heat cracking resistance, planar part anti-corrosion property, corrosion resistance after alkali degreasing, blackening resistance, stack blackening resistance, anti-water stain property, solvent resistance, perspiration resistance, coating adhesion property, and storage stability. The disclosed surface-treatment solution contains a glycidyl group-containing silane coupling agent (A), a tetraalkoxysilane (B), a zirconium carbonate compound (C), and an anionic polyurethane resin (D) having a glass transition temperature (Tg) of 80° C. to 130° C., a vanadium compound (E), a molybdic acid compound (F), and water, the surface-treatment solution having a pH of 8.0 to 10.0, and the amount of each component satisfying a predetermined relationship.