Abstract: The invention relates to uses of glasses and glass-ceramics in dental and orthodontic applications.

Abstract: A polycrystalline translucent aluminum oxide ceramic material having an average grain size of no greater than 1.0 micron and a Contrast Ratio value of less than about 0.7. The material can be in the form of a dental mill blank, dental prosthesis or other dental article or non-dental article.

Abstract: The inventive dental composition comprises (a) a part A comprising at least one polyacid and at least one polymerizable component; and (b) a part B comprising water, wherein the composition further comprises an oxidizing agent, a reducing agent, and reactive fillers in at least one of part A or part B and wherein at least one of the polyacid, oxidizing agent, and reducing agent is in a disperse phase. The dental composition can be used in many dental applications and is particularly suited for use as a cement.

Abstract: The invention relates to uses of glasses and glass-ceramics in dental and orthodontic applications.

Abstract: A curable slurry for forming ceramic microstructures on a substrate using a mold. The slurry is a mixture of a ceramic powder, a fugitive binder, and a diluent. The ceramic powder has a low softening temperature in a range of about 400° C. to 600° C. and a coefficient of thermal expansion closely matched to that of the substrate. The fugitive binder is capable of radiation curing, electron beam curing, or thermal curing. The diluent promotes release properties with the mold after curing the binder or quick and complete burn out of the binder during debinding.

Abstract: An orthodontic appliance that includes a polycrystalline translucent aluminum oxide ceramic material having an average grain size of no greater than 1.0 micron and a Contrast Ratio value of less than about 0.7.

Abstract: The present invention provides a dental paste, a dental article, methods of making and using the dental paste, and compositions prepared therefrom. In one embodiment, the dental paste includes (a) a filler including porous, non-pyrogenic silica having a silane treated surface and being substantially free of heavy metals and (b) a filler including non-aggregated primary silica particles, with the fillers being dispersed in a hardenable resin.

Abstract: An orthodontic appliance that includes a polycrystalline translucent aluminum oxide ceramic material having an average grain size of no greater than 1.0 micron and a Contrast Ratio value of less than about 0.7.

Abstract: Polymerizable compositions that include: (a) a cationically active functional group; (b) an initiation system capable of initiating cationic polymerization of the cationically active functional group; and (c) a filler composition that includes various radiopacifying fillers in an amount sufficient to render the polymerizable composition radiopaque. Components (a), (b), and (c) are selected such that the polymerizable composition polymerizes to form a polymerized composition having a Barcol hardness, measured using a GYZJ-935 meter, of at least 10 within 30 minutes following initiation of the cationically active functional group at a reaction temperature of 25° C.

Abstract: A dental mill blank comprising a resin and a filler, wherein the blank is fabricated such that it passes a Thermal Shock Test. The mill blank is substantially free of cracks and discontinuities. Further, the blank may have superior cuttability and hardness.

Abstract: A polycrystalline translucent aluminum oxide ceramic material having an average grain size of no greater than 1.0 micron and a Contrast Ratio value of less than about 0.7. The material can be in the form of a dental mill blank, dental prosthesis or other dental article or non-dental article.

Abstract: An apparatus and method of use that include a dental model, a support that includes a mounting surface and a stretch release pressure sensitive adhesive located between the dental model and the support. The stretch release pressure sensitive adhesive attaches the dental model to the mounting surface. In an additional embodiment, a highly extensible and substantially inelastic backing having a layer of the stretch release pressure sensitive adhesive is used to attach the dental model to the mounting surface. The dental model and the support are separated without damage by stretching the stretch release pressure sensitive adhesive at an angle no greater than about 35 degrees from the mounting surface.

Abstract: This invention provides light transmissive crystalline ceramic dental mill blanks and prostheses having a Contrast Ratio value of less than about 0.7. The dental mill blank is suitable for fabricating into an aesthetic restoration or prosthesis.

Abstract: The inventive dental composition comprises (a) a part A comprising at least one polyacid and at least one polymerizable component; and (b) a part B comprising water, wherein the composition further comprises an oxidizing agent, a reducing agent, and reactive fillers in at least one of part A or part B and wherein at least one of the polyacid, oxidizing agent, and reducing agent is in a disperse phase. The dental composition can be used in many dental applications and is particularly suited for use as a cement.

Abstract: Polymerizable composition that include: (a) a cationically active functional group; (b) an initiation system capable of initiating cationic polymerization of the cationically active functional group; and (c) a filler composition that includes various radiopacifying fillers in an amount sufficient to render the polymerizable composition radiopaque. Components (a), (b), and (c) are selected such that the polymerizable composition polymerizes to form a polymerized composition having a Barcol hardness, measured using a GYZJ-935 meter, of at least 10 within 30 minutes following initiation of the cationically active functional group are a reaction temperature of 25° C.

Abstract: The present invention provides a multiple part ionomeric cement system comprising an organic composition that is substantially free of added water, and an aqueous composition comprising water. The organic composition contains at least a hydrophilic component and an acid functional compound that is provided as greater than 1.0% weight of the organic composition. The liquid ingredients of the compositions are miscible, both as separate compositions and when mixed together.

Abstract: A curable slurry for forming ceramic microstructures on a substrate using a mold. The slurry is a mixture of a ceramic powder, a fugitive binder, and a diluent. The ceramic powder has a low softening temperature in a range of about 400° C. to 600° C. and a coefficient of thermal expansion closely matched to that of the substrate. The fugitive binder is capable of radiation curing, electron beam curing, or thermal curing. The diluent promotes release properties with the mold after curing the binder or quick and complete burn out of the binder during debinding.

Abstract: A dental mill blank comprising a resin and a filler, wherein the blank is fabricated such that it passes a Thermal Shock Test. The mill blank is substantially free of cracks and discontinuities. Further, the blank may have superior cuttability and hardness.

Abstract: A curable slurry for forming ceramic microstructures on a substrate using a mold. The slurry is a mixture of a ceramic powder, a fugitive binder, and a diluent. The ceramic powder has a low softening temperature in a range of about 400° C. to 600° C. and a coefficient of thermal expansion closely matched to that of the substrate. The fugitive binder is capable of radiation curing, electron beam curing, or thermal curing. The diluent promotes release properties with the mold after curing the binder or quick and complete burn out of the binder during debinding.

Abstract: Polymerizable composition that include: (a) a cationically active functional group; (b) an initiation system capable of initiating cationic polymerization of the cationically active functional group; and (c) a filler composition that includes various radiopacifying fillers in an amount sufficient to render the polymerizable composition radiopaque. Components (a), (b), and (c) are selected such that the polymerizable composition polymerizes to form a polymerized composition having a Barcol hardness, measured using a GYZJ-935 meter, of at least 10 within 30 minutes following initiation of the cationically active functional group are a reaction temperature of 25° C.