Abstract: The coating the tungsten powder particles with a ceramic barrier suppresses the leachability of tungsten in aqueous media. Preferably, the ceramic coating substantially encapsulates each particle of tungsten and has a thickness of at least about 30 nm and, more preferable, from about 200 nm to about 500 nm. Examples of ceramic coatings that may be used include, but are not limited to, aluminum oxide (alumina), aluminum oxyhydroxide (AlOOH), zirconium oxide (zirconia), cerium oxide (ceria), hafnium oxide (hafnia), and magnesium oxide (magnesia).

Abstract: The interaction of Sn, Sb and Pb with tungsten in contact with an aqueous medium has a synergistic effect in which the leachability of each metal is suppressed. This means that tungsten has the ability to suppress the leachability of these same metals, in particular lead. For example, tungsten may be added to the lead-contaminated soil in order to suppress lead contamination of the ground water by forming lead tungstate which has a very low solubility.

Abstract: The leachability of tungsten in an aqueous medium may be suppressed by combining tungsten metal with a metal oxide or metal salt that will form an insoluble tungsten-containing compound when the mixture is brought into contact with an aqueous medium. The additive is preferably present in an amount from about 1 weight percent (wt. %) to about 10 weight percent of the tungsten of the tungsten. Preferred additives are lead oxide and calcium sulfate.