Abstract: The invention concerns an extruded, rolled and/or forged aluminum-based alloy product having a thickness of at least 25 mm comprising (in weight %): Zn 6.70-7.40; Mg 1.50-1.80; Cu 2.20-2.60, with a Cu to Mg ratio of at least 1.30; Zr 0.04-0.14; Mn 0-0.5; Ti 0-0.15; V 0-0.15; Cr 0-0.25; Fe 0-0.15; Si 0-0.15; impurities ?0.05 each and ?0.15 total. The invention also concerns a method of making such a product. Products according to the invention are particularly advantageous because they exhibit simultaneously a low sensitivity to environmentally assisted cracking under conditions of high stress and humid environment, high strength and high toughness properties.

Abstract: The invention relates to a rolled product made of aluminum alloy with a thickness of at least 50 mm comprising (in weight %): Zn 6.9-7.5; Mg 1.8-2.2; Cu 1.8-2.2, where the sum Cu+Mg is between 3.8 and 4.2; Zr 0.04-0.14; Mn 0-0.1; Ti 0-0.15; V 0-0.1; Fe?0.15; If ?0.15; impurities ?0.05 each and ?0.15 total, balance aluminum. The invention also relates to the method of manufacturing such a product. The products according to the invention are particularly advantageous because they have a very favorable compromise between static mechanical strength, toughness and environmental-assisted cracking performance under conditions of high stress and humid environment.

Abstract: The invention relates to a rolled aluminum-based alloy product having a thickness of at least 80 mm comprising, (in weight %): Zn 6.85-7.25, Mg 1.55-1.95, Cu 1.90-2.30, Zr 0.04-0.10, Ti 0-0.15, Fe 0-0.15, Si 0-0.15, other elements ?0.05 each and ?0.15 total, remainder Al, wherein at mid-thickness more than 75% of grains are recrystallized or at mid-thickness 30 to 75% of grains are recrystallized and non-recrystallized grains have an aspect ratio in a L/ST cross section less than 3. A process for the manufacture of a rolled aluminum-based alloy product comprises the steps of: (a) casting an ingot made in an alloy according to the invention, (b) conducting an homogenization of the ingot (c) conducting hot rolling of said homogenized ingot in one or more stages by rolling, (d) conducting a solution heat treatment a quench, (e) conducting stress relieving, and, (f) conducting an artificial aging treatment.

Abstract: The invention relates to a rolled product made of aluminum alloy with a thickness of at least 50 mm comprising (in weight %): Zn 6.9-7.5; Mg 1.8-2.2; Cu 1.8-2.2, where the sum Cu+Mg is between 3.8 and 4.2; Zr 0.04-0.14; Mn 0-0.1; Ti 0-0.15; V 0-0.1; Fe?0.15; If?0.15; impurities ?0.05 each and ?0.15 total, balance aluminum. The invention also relates to the method of manufacturing such a product. The products according to the invention are particularly advantageous because they have a very favorable compromise between static mechanical strength, toughness and environmental-assisted cracking performance under conditions of high stress and humid environment.

Abstract: An aluminium alloy comprising lithium with improved mechanical strength and toughness. The invention relates to a 2XXX wrought alloy product comprising from 0.05 to 1.9% by weight of Li and from 0.005 to 0.045% by weight of Cr and/or of V. The invention also relates to an as-cast 2XXX alloy product comprising from 0.05 to 1.9% by weight of Li and from 0.005 to 0.045% by weight of Cr and/or of V. Finally, the invention relates to an aircraft structure element, preferably a lower surface or upper surface element, the skin and stiffeners of which originate from the same starting material, a spar or a rib, comprising a wrought product.

Abstract: The invention concerns an extruded, rolled and/or forged aluminum-based alloy product having a thickness of at least 25 mm comprising (in weight %): Zn 6.70-7.40; Mg 1.50-1.80; Cu 2.20-2.60, with a Cu to Mg ratio of at least 1.30; Zr 0.04-0.14; Mn 0-0.5; Ti 0-0.15; V 0-0.15; Cr 0-0.25; Fe 0-0.15; Si 0-0.15; impurities ?0.05 each and ?0.15 total. The invention also concerns a method of making such a product. Products according to the invention are particularly advantageous because they exhibit simultaneously a low sensitivity to environmentally assisted cracking under conditions of high stress and humid environment, high strength and high toughness properties.

Abstract: The invention is a rolled and/or forged product, made of an aluminium-based alloy comprising, in % by weight, Cu: 3.2-4.0; Li: 0.80-0.95; Zn: 0.45-0.70; Mg: 0.15-0.7; Zr: 0.07-0.15; Mn: 0.1-0.6; Ag:<0.15; Fe+Si?0.20; at least one element from Ti: 0.01-0.15; Se: 0.02-0.1; Cr: 0.02-0.1; Hf: 0.02-0.5; V: 0.02-0.1; other elements ?0.05 each and ?0.15 in total, remainder aluminium. In the process for manufacturing the products according to the invention a bath of liquid metal based on aluminium as alloy according to the invention is melted, an unwrought product is cast from said bath of liquid metal; said unwrought product is homogenized at a temperature between 450° C. and 550° C.; said unwrought product is hot worked and optionally cold worked preferably to a thickness of at least 15 mm: said product is solution treated between 490° C. and 530° C.