Abstract: In accordance with an exemplary embodiment, a method of forming a oxide dispersion-strengthened alloy metal includes the steps of providing, in a powdered form, an oxide dispersion-strengthened alloy composition that is capable of achieving a dispersion-strengthened microstructure, directing a low energy density energy beam at a portion of the alloy composition, withdrawing the energy beam from the portion of the powdered alloy composition, and cooling the portion of the powdered alloy composition at a rate greater than or equal to about 106° F. per second, thereby forming the oxide dispersion-strengthened alloy metal.

Abstract: In accordance with an exemplary embodiment, a method of forming a oxide dispersion-strengthened alloy metal includes the steps of providing, in a powdered form, an oxide dispersion-strengthened alloy composition that is capable of achieving a dispersion-strengthened microstructure, directing a low energy density energy beam at a portion of the alloy composition, withdrawing the energy beam from the portion of the powdered alloy composition, and cooling the portion of the powdered alloy composition at a rate greater than or equal to about 106° F. per second, thereby forming the oxide dispersion-strengthened alloy metal.

Abstract: A cast iron alloy composition comprising 2.5-3.5% carbon, 0.5-1.0% manganese, 0.25-1.5% silicon, 13-19% chromium, 0.8-3.0% nickel, balance essentially iron which is machinable in the annealed condition and abrasion resistant in the hardened condition. The alloy may be annealed by furnace cooling, at a rate between 100.degree. C. and 350.degree. C./hr., from the austenitizing temperature, and hardened by air cooling from the austenitizing temperature.