Abstract: A copper core used in electroformed metal (EFM) masks is replaced with a copper/molybdenum/copper clad core (Cu/Mo/Cu). The copper cladding on the molybdenum enhances adhesion of electroplated nickel. The nickel is electro-deposited through a patterned resist template onto the copper clad molybdenum surface. The copper and molybdenum are etched by selective etchants that do not attack other non-etched layers, leaving a patterned nickel stencil on a high-strength supporting base.

Abstract: A method of making, and the resultant mask, comprises developing resist layers over surfaces of a masking layer to transfer significantly reduced sized openings within glass masters attached to the surfaces of the masking layer into the resist layers. These significantly reduced sized openings within the resist layers are then transferred into the masking layer within a first etch bath by simultaneously monitoring and controlling both etchant activity and concentration of a byproduct within the etch bath formed between the masking material and the etchant. The openings may be etched to completion within the first etch bath, or alternatively, the openings may be etched to a pre-finished image size. Wherein the openings are etched to a pre-finished image size, the masking layer is immersed into a second etch bath for further micro-etching of these openings to a final desired image size.

Abstract: Disclosed is a method of manufacturing a metal mask for an integrated circuit chip interconnect solder bump. The invention deposits a very thick photoresist on both sides of a very thick molybdenum foil sheet (the molybdenum sheet is at least 8 mils thick and the photoresist is at least 5 microns thick). Then the process exposes and develops the photoresist to produce at least one opening having a diameter of at least 5 mil. The invention simultaneously etches both sides of the molybdenum foil using a very low etchant spray pressure of approximately 5 psi to form at least one via in the molybdenum foil that has a diameter of at least 12 mil and a knife-edge of 0.2 mil. The photoresist is removed after the etching process.