Abstract: A hot-rolled strip steel product having a chemical composition consisting of, in terms of weight percentages (wt. %): 0.025%-0.070% C, 0%-1.10% Si, 0.50%-2.0% Mn, <0.020% P, <0.050% S, <0.010% N, 0%-0.60% Cr, 0%-0.20% Ni, 0%-0.25% Cu, 0%-0.20% Mo, 0%-0.15% Al, 0%-0.050% Nb, 0.020%-0.20-% V, 0.020%-0.15% Ti, 0%-0.0010% B, remainder Fe and inevitable impurities, wherein the strip steel product has a microstructure comprising of, in terms of volume percentages (vol. %), ferrite ?90%, wherein the ferrite structure comprises 10%-50% quasi-polygonal ferrite and a reminder of ferrite structure is polygonal ferrite and/or bainite: and wherein the steel strip product has an average ferrite grain size of <10 ?m, an average hole expansion ratio of ?50%, a yield strength (Rp0.2%) longitudinal to rolling direction of ?660 MPa and a tensile strength of ?760 MPa.

Abstract: Described is a hot-rolled steel strip product having a tensile strength (Rm) above 1400 MPa and a microstructure that includes at least 90% by volume of martensite. The steel has a composition includes, in percent by weight (wt.-%): C 0.20-0.26 Si 0.05-0.5, Mn 0.2-0.8, Cr 0.2-0.6, Ni 0.2-0.5, Al 0.015-0.065, Ti 0.005-0.02, B 0.001-0.005, optionally Mo<0.10, optionally Nb<0.01, optionally V<0.04, balance Fe and unavoidable impurities.

Abstract: A hot-rolled strip steel product is described having a chemical composition consisting of, in terms of weight percentages (wt. %): 0.030%-0.10% C, 0%-1.10% Si, 0.50%-2.0% Mn, <0.020% P, <0.010% S, <0.010% N, 0%-0.60% Cr, 0%-0.20% Ni, 0%-0.25% Cu, 0%-0.30% Mo, 0%-0.15% Al, 0%-0.10% Nb, 0.10%-0.30% V, <0.020% Ti, 0%-0.0010% B, remainder being Fe and inevitable impurities, wherein the hot rolled strip steel product has a a microstructure comprising, in terms of volume percentages (vol. %), ferrite?90, wherein the ferrite structure comprises bainite, at least 50% of polygonal ferrite and at most 10% quasi-polygonal ferrite, and wherein the steel strip product has an average hole expansion ratio?50%, a yield strength (Rp0.2%) longitudinal to rolling direction of ?660 MPa and a tensile strength?760 MPa.

Abstract: A hot-rolled strip steel product is described having a chemical composition consisting of, in terms of weight percentages (wt. %): 0.030%-0.10% C, 0%-1.10% Si, 0.50%-2.0% Mn, <0.020% P, <0.010% S,<0.010% N, 0%-0.60% Cr, 0%-0.20% Ni, 0%-0.25% Cu, 0%-0.30% Mo, 0%-0.15% Al, 0%-0.10% Nb, 0.10%-0.30% V, <0.020% Ti, 0%-0.0010% B, remainder being Fe and inevitable impurities, wherein the hot rolled strip steel product has a a microstructure comprising, in terms of volume percentages (vol. %), ferrite?90, wherein the ferrite structure comprises bainite, at least 50% of polygonal ferrite and at most 10% quasi-polygonal ferrite, and wherein the steel strip product has an average hole expansion ratio?50%, a yield strength (Rp0.2%) longitudinal to rolling direction of ?660 MPa and a tensile strength?760 MPa.

Abstract: A hot-rolled strip steel product having a chemical composition consisting of, in terms of weight percentages (wt. %): 0.025%-0.070% C, 0%-1.10% Si, 0.50%-2.0% Mn, <0.020% P, <0.050% S, <0.010% N, 0%-0.60% Cr, 0%-0.20% Ni, 0%-0.25% Cu, 0%-0.20% Mo, 0%-0.15% Al, 0%-0.050% Nb, 0.020%-0.20-% V, 0.020%-0.15% Ti, 0%-0.0010% B, remainder Fe and inevitable impurities, wherein the strip steel product has a microstructure comprising of, in terms of volume percentages (vol. %), ferrite ?90%, wherein the ferrite structure comprises 10%-50% quasi-polygonal ferrite and a reminder of ferrite structure is polygonal ferrite and/or bainite: and wherein the steel strip product has an average ferrite grain size of <10 ?m, an average hole expansion ratio of ?50%, a yield strength (Rp0.2%) longitudinal to rolling direction of ?660 MPa and a tensile strength of ?760 MPa.