Abstract: A process for manufacturing chromenes intended for the preparation of thermosetting resins, includes transforming an aromatic propargyl ether of general formula (I) into a chromene by homogeneous gold(I) catalysis with the catalyst (acetonitrile)[(2-biphenyl)di-tert-butylphosphine]gold(I) hexafluoroantimonate in an organic solvent under an inert or non-inert atmosphere. Moreover, a process for preparing a material made of thermoset resin, includes successively a) implementation of the above process; polymerization of the reaction product obtained in step a) so as to obtain the material made of thermoset resin; c) recovery of the material made of thermoset resin obtained in step b).

Abstract: A process for producing chromenes intended for the preparation of thermosetting resins, includes converting an aromatic propargyl ether of general formula (I) into a chromene by homogeneous catalysis with copper salts in anisole at a temperature between 100 and 170° C. Moreover, a process for preparing a material made of thermoset resin, includes successively a) carrying out the above process; b) polymerizing the reaction product obtained in a) so as to obtain the material made of thermoset resin; c) recovering the material made of thermoset resin obtained in b).

Abstract: A process for manufacturing chromenes which are intended for the preparation of thermosetting resins, includes transforming an aromatic propargyl ether of general formula (I) into a chromene by flash vacuum thermolysis, at a temperature of between 300 and 600° C., at a pressure of between 4 and 10,000 Pa. It also concerns a process for preparing a material made of thermoset resin, including successively: a) implementation of the above process; b) polymerization of the reaction product obtained in a) so as to obtain the material made of thermoset resin; c) recovery of the material made of thermoset resin obtained in b).

Abstract: A process for manufacturing chromenes which are intended for the preparation of thermosetting resins, includes transforming an aromatic propargyl ether of general formula (I) into a chromene by flash vacuum thermolysis, at a temperature of between 300 and 600° C., at a pressure of between 4 and 10 000 Pa. It also concerns a process for preparing a material made of thermoset resin, including successively: a) implementation of the above process; b) polymerization of the reaction product obtained in a) so as to obtain the material made of thermoset resin; c) recovery of the material made of thermoset resin obtained in b).

Abstract: A process for manufacturing chromenes intended for the preparation of thermosetting resins, includes transforming an aromatic propargyl ether of general formula (I) into a chromene by homogeneous gold(I) catalysis with the catalyst (acetonitrile)[(2-biphenyl)di-tert-butylphosphine]gold(I) hexafluoroantimonate in an organic solvent under an inert or non-inert atmosphere. Moreover, a process for preparing a material made of thermoset resin, includes successively a) implementation of the above process; polymerization of the reaction product obtained in step a) so as to obtain the material made of thermoset resin; c) recovery of the material made of thermoset resin obtained in step b).

Abstract: A process for producing chromenes intended for the preparation of thermosetting resins, includes converting an aromatic propargyl ether of general formula (I) into a chromene by homogeneous catalysis with copper salts in anisole at a temperature between 100 and 170° C. Moreover, a process for preparing a material made of thermoset resin, includes successively a) carrying out the above process; b) polymerizing the reaction product obtained in a) so as to obtain the material made of thermoset resin; c) recovering the material made of thermoset resin obtained in b).