Abstract: Polymers, hydrogels, and thermochromic agents, including products embodying them, methods of using them, and processes for making them. In certain embodiments, temperature therapy packs which utilize thermochromic agents integrated into solid, semi-solid, or liquid hydrogels. In preferred (but optional) embodiments, the thermochromic agents are integrated into the composition used as the temperature exchange material of the therapy pack. In certain other embodiments, methods of using the thermochromic integrated temperature exchange materials, or processes for manufacturing such thermochromic integrated temperature exchange materials and/or methods or processes for manufacturing or using thermal packs embodying such materials. In certain particularly preferred embodiments, novel polymer compositions and/or processes for making polymers, which improve product durability or longevity and/or which improve use cycles or usage times.

Abstract: Polymers, hydrogels, and thermochromic agents, including products embodying them, methods of using them, and processes for making them. In certain embodiments, temperature therapy packs which utilize thermochromic agents integrated into solid, semi-solid, or liquid hydrogels. In preferred (but optional) embodiments, the thermochromic agents are integrated into the composition used as the temperature exchange material of the therapy pack. In certain other embodiments, methods of using the thermochromic integrated temperature exchange materials, or processes for manufacturing such thermochromic integrated temperature exchange materials and/or methods or processes for manufacturing or using thermal packs embodying such materials. In certain particularly preferred embodiments, novel polymer compositions and/or processes for making polymers, which improve product durability or longevity and/or which improve use cycles or usage times.

Abstract: Polymers, hydrogels, and thermochromic agents, including products embodying them, methods of using them, and processes for making them. In certain embodiments, temperature therapy packs which utilize thermochromic agents integrated into solid, semi-solid, or liquid hydrogels. In preferred (but optional) embodiments, the thermochromic agents are integrated into the composition used as the temperature exchange material of the therapy pack. In certain other embodiments, methods of using the thermochromic integrated temperature exchange materials, or processes for manufacturing such thermochromic integrated temperature exchange materials and/or methods or processes for manufacturing or using thermal packs embodying such materials. In certain particularly preferred embodiments, novel polymer compositions and/or processes for making polymers, which improve product durability or longevity and/or which improve use cycles or usage times.

Abstract: CPVC pipe in diameters in the range from 15 mm (0.5 inch) to 15.24 cm (6 ins), to carry hot and cold aqueous streams under 690 KPa (100 psi) pressure and 82.2° C. (180° F.) in continuous service, is extruded from a compound in which the CPVC has a high Cl content in the range from 66.5%-70%, when modified with either of two specific impact high rubber modifiers in an amount greater than 5 parts but no more than 6 parts per 100 parts of CPVC. Extruded CPVC pipe provides a HDB measured according to ASTM D2837-01 which is 25% or more greater than that required for commercial pipe as specified in ASTM D2846. As a result, both SDR-11 and SDR-13.5 pipe are produced which provide a HDB of at least 1250 psi (8.62 MPa) at the 100,000 hr intercept.

Abstract: CPVC pipe in diameters in the range from 15 mm (0.5 inch) to 15.24 cm (6 ins), to carry hot and cold aqueous streams under 690 KPa (100 psi) pressure and 82.2° C. (180° F.) in continuous service, is extruded from a compound in which the CPVC has a high Cl content in the range from 66.5%-70%, when modified with either of two specific impact high rubber modifiers in an amount greater than 5 parts but no more than 6 parts per 100 parts of CPVC. Extruded CPVC pipe provides a HDB measured according to ASTM D2837-01 which is 25% or more greater than that required for commercial pipe as specified in ASTM D2846. As a result, both SDR-11 and SDR-13.5 pipe are produced which provide a HDB of at least 1250 psi (8.62 MPa) at the 100,000 hr intercept.

Abstract: CPVC pipe in diameters in the range from 15 mm (0.5 inch) to 15.24 cm (6 ins), to carry hot and cold aqueous streams under 690 KPa (100 psi) pressure and 82.2° C. (180° F.) in continuous service, is extruded from a compound in which the CPVC has a high Cl content in the range from 66.5%-70%, when modified with either of two specific impact high rubber modifiers in an amount greater than 5 parts but no more than 6 parts per 100 parts of CPVC. Extruded CPVC pipe provides a HDB measured according to ASTM D2837-01 which is 25% or more greater than that required for commercial pipe as specified in ASTM D2846. As a result, both SDR-11 and SDR-13.5 pipe are produced which provide a HDB of at least 1250 psi (8.62 MPa) at the 100,000 hr intercept.