Abstract: A group of reductive 2D materials (R2D) with extended reactive vacancies and a method for making the R2D with extended reactive vacancies are provided, especially the example of the reductive boron nitride (RBN). To create defects such as vacancies, boron nitride (BN) powders are milled at cryogenic temperatures. Vacancies are produced by milling, and the vacancies can be used to reduce various metal nanostructures on RBN. Due to the thermal stability of the RBN and the enhanced catalytic performance of metal nanostructures, RBN-metals can be used for different catalysts, including electrochemical catalysts and high temperature catalysts.

Abstract: Provided is a water treatment flow channel member in which the occurrence of fouling is suppressed. A water treatment flow channel member 1 of the present invention is formed from a molded product containing a synthetic resin and a nanocarbon material.

Abstract: We report a method of preparation of highly elastic graphene oxide films, and their transformation into graphene oxide fibers and electrically conductive graphene fibers by spinning. Methods typically include: 1) oxidation of graphite to graphene oxide, 2) preparation of graphene oxide slurry with high solid contents and residues of sulfuric acid impurities. 3) preparation of large area films by bar-coating or dropcasting the graphene oxide dispersion and drying at low temperature. 4) spinning the graphene oxide film into a fiber, and 5) thermal or chemical reduction of the graphene oxide fiber into an electrically conductive graphene fiber. The resulting films and fiber have excellent mechanical properties, improved morphology as compared with current graphene oxide fibers, high electrical conductivity upon thermal reduction, and improved field emission properties.

Abstract: We report a method of preparation of highly elastic graphene oxide films, and their transformation into graphene oxide fibers and electrically conductive graphene fibers by spinning. Methods typically include: 1) oxidation of graphite to graphene oxide, 2) preparation of graphene oxide slurry with high solid contents and residues of sulfuric acid impurities. 3) preparation of large area films by bar-coating or dropcasting the graphene oxide dispersion and drying at low temperature. 4) spinning the graphene oxide film into a fiber, and 5) thermal or chemical reduction of the graphene oxide fiber into an electrically conductive graphene fiber. The resulting films and fiber have excellent mechanical properties, improved morphology as compared with current graphene oxide fibers, high electrical conductivity upon thermal reduction, and improved field emission properties.

Abstract: A method of reducing a film of graphite oxide. In one embodiment, the method includes the steps of providing a film of graphite oxide with a thickness d0; and delivering optical energy in a single pulse to the film of graphite oxide at a distance no more than 1.0 cm away from the film of graphite oxide to reduce the film of graphite oxide to a film of graphene with a thickness d, wherein the optical energy has a radiant exposure in the range of between 0.1 and 2 J/cm2, and wherein the thickness d is greater than the thickness d0. In one embodiment, the thickness d?10×d0.

Abstract: A method of reducing a film of graphite oxide. In one embodiment, the method includes the steps of providing a film of graphite oxide with a thickness d0; and delivering optical energy in a single pulse to the film of graphite oxide at a distance no more than 1.0 cm away from the film of graphite oxide to reduce the film of graphite oxide to a film of graphene with a thickness d, wherein the optical energy has a radiant exposure in the range of between 0.1 and 2 J/cm2, and wherein the thickness d is greater than the thickness d0. In one embodiment, the thickness d?10×d0.