Abstract: A method for treating lignin containing pulp, subsequent to being bleached by:a) always treated with at least one chemical, which chemically reduces .alpha.-carbonyl and .gamma.-carbonyl groups in the lignin; and in at least one further step isb) treated with at least one chemical, which will block the phenolic hydroxyl groups of the lignin and/orc) supplied with at least one chemical, which will convert short-wave light quanta to long-wave light quanta.According to a preferred embodiment of the invention cellulose pulp is subjected to all of the above treatment processes, i.e. a)+b)+c) and is washed after the two initial treatment stages. The method solves the problem of yellowing of lignin containing pulps, e.g. high yield pulp.

Abstract: Chemimechanical pulp is produced from lignocellulosic material in a process in which the material is impregnated in two stages. The material is treated in the first stage with alkaline and, subsequent to passing an intermediate draining and reaction step, in the second stage with a solution that contains peroxide. The quantities of alkali and peroxide charged are fully optional and are independent of one another. The material is then optionally subjected to a further drainage and reaction step, and thereafter pre-heated at a temperature of between 50.degree. C. and 100.degree. C., whereafter the material is refined in one or two stages.The optimal brightness of the processed pulp for a given peroxide consumption is achieved by a balanced division of the peroxide charge between chip impregnation and bleaching.

Abstract: In accordance with the invention a chemimechanical pulp is produced from lignocellulosic material, for example wood chips, by subjecting the material to a process in which it is steamed, impregnated with alkali and peroxide, drained, pre-heated, refined and bleached. The material is impregnated in a single stage with a solution containing alkali and peroxide. Subsequent to passing an intermediate drainage and reaction stage, the material is pre-heated to a temperature of from about 50.degree. C., but not above 100.degree. C. The material is then refined in one or two stages. The material can be impregnated by immersing the same in the impregnating solution for a period of up to 20 minutes at a temperature of 15.degree.-60.degree. C., or by compressing the material in a screw press and permitting the compressed material to expand in the impregnating solution.