Abstract: A coated superalloy article is prepared by furnishing a nickel-base superalloy article substrate having a rhenium content of not less than about 4.0 percent by weight, and thereafter depositing an aluminum-containing coating onto a surface of the article substrate. The aluminum-containing coating includes an additive zone having an average aluminum content of not greater than about 27 percent by weight, and a diffusion zone of interdiffusion with the article substrate. A ratio of a thickness of the additive zone to a thickness of the diffusion zone is not greater than about 3:1, and is preferably about 1:1.

Abstract: A coated nickel-base superalloy article, which is otherwise susceptible to the formation of a secondary reaction zone, is prepared by furnishing a nickel-base superalloy article substrate having thereon an initial aluminum-containing coating comprising an initial-coating additive zone and an initial-coating diffusion zone. The article is susceptible to the formation of the secondary reaction zone if heated to an elevated SRZ reaction temperature for an SRZ reaction period of time. The formation of the secondary reaction zone is avoided by first removing the initial-coating additive zone and the initial-coating diffusion zone, and thereafter depositing a subsequent aluminum-containing coating onto the article substrate. The subsequent aluminum-containing coating includes a subsequent-coating additive zone and a subsequent-coating diffusion zone.

Abstract: A coated superalloy article is prepared by furnishing a nickel-base superalloy article substrate having a rhenium content of not less than about 4.0 percent by weight, and thereafter depositing an aluminum-containing coating onto a surface of the article substrate. The aluminum-containing coating includes an additive zone having an average aluminum content of not greater than about 27 percent by weight, and a diffusion zone of interdiffusion with the article substrate. A ratio of a thickness of the additive zone to a thickness of the diffusion zone is not greater than about 3:1, and is preferably about 1:1.

Abstract: A coated nickel-base superalloy article, which is otherwise susceptible to the formation of a secondary reaction zone, is prepared by furnishing a nickel-base superalloy article substrate having thereon an initial aluminum-containing coating comprising an initial-coating additive zone and an initial-coating diffusion zone. The article is susceptible to the formation of the secondary reaction zone if heated to an elevated SRZ reaction temperature for an SRZ reaction period of time. The formation of the secondary reaction zone is avoided by first removing the initial-coating additive zone and the initial-coating diffusion zone, and thereafter depositing a subsequent aluminum-containing coating onto the article substrate. The subsequent aluminum-containing coating includes a subsequent-coating additive zone and a subsequent-coating diffusion zone.