Abstract: Process for manufacturing a galvanized steel sheet, comprising steps of coating a steel sheet with nickel in an amount of from 0.2 to 2 g/m.sup.2, heating the steel sheet thus coated to a temperature within the range of from 420.degree. C. to 500.degree. C. in a non-oxidative atmosphere, and dipping the nickel coated steel sheet into a molten zinc bath containing aluminum at a content of from 0.1 to 1% without contact with air, wherein the steel sheet is dipped into the molten zinc bath within 15 seconds after the temperature of the steel sheet exceeds 350.degree. C. in the heating step.

Abstract: Process for manufacturing a galvanized steel sheet, comprising steps of coating a steel sheet with nickel in an amount of from 0.2 to 2 g/m.sup.2, heating the steel sheet thus coated to a temperature within the range of from 420.degree. C. to 500.degree. C. in a non-oxidative atmosphere, and dipping the nickel coated steel sheet into a molten zinc bath containing aluminum at a content of from 0.1 to 1% without contract with air, wherein the steel sheet is dipped into the molten zinc bath within 15 seconds after the temperature of the steel sheet extends 350.degree. C. in the heating step.

Abstract: An anode system for plasma heating usable in the tundish of a continuous casting apparatus, which is economical and simple in structure and can enjoy a long service life, and comprises a dam member provided on the bottom surface of a tundish near and along a side wall or an over-flow wall of the tundish to form a space or gap therebetween, an electrical conductive member with its end portion exposed to the space or gap and the other end electrically connected to a power source, said dam member having a height higher than a level of molten metal remaining after the pouring of the molten metal from the tundish, but lower than a minimum level of molten metal normally contained in the tundish.