Abstract: A barrier composite film comprises a base film, an anchor coat layer, an inorganic layer such as a silicon oxide layer, and a coating layer containing a silane coupling agent and a barrier resin (e.g. a vinylidene chloride-series copolymer, an ethylene-vinyl alcohol copolymer), the layers being formed on at least one side of the base film in the order of reference. The anchor coat layer can be made of (A) a chlorine-containing resin such as a vinyl chloride-vinyl acetate copolymer, (B) a polyisocyanate compound, and (C) a saturated polyester resin having a glass transition temperature of -10.degree. C. to 20.degree. C. and being substantially unreactive to the component (B). A heat-sealing layer may be formed on the surface of the coating layer or the other side of the base film. This composite film provided with the inorganic layer can avoid a loss of its adhesive properties and barrier properties even under severe conditions such as retort treatment.

Abstract: At least one side of a base film is successively covered with an anchor coat layer comprising (A) a chlorine-containing resin e.g. a vinyl chloride-vinyl acetate copolymer, (B) a polyisocyanate compound and (C) a saturated polyester resin having glass transition temperature of -10.degree. C. to 20.degree. C. and being substantially unreactive to the polyisocyanate compound, and an inorganic layer such as a silicon oxide. The component (C) includes a noncrystalline saturated polyesters each having a hydroxyl value of 0 to 15 mg KOH/g or acid value of 0 to 10 mg KOH/g. The anchor coat layer may comprise about 10 to 500 parts by weight of the component (B) and 1 to 50 parts by weight of the component (C) relative to 100 parts by weight of the component (A). Such composite film inhibits deterioration of the adhesive properties and barrier properties even when exposed to severe conditions such as retort treatment.

Abstract: At least one side of a polyester or other base film is successively covered with an inorganic layer composed of a silicon oxide or the like and a coating layer comprising a silane coupling agent and a barrier resin (e.g. vinylidene chloride-based copolymer, ethylene-vinyl alcohol copolymer) to provide a barrier composite film. The amount of the silane coupling agent is about 0.05 to 10 parts by weight relative to 100 parts by weight of the barrier resin. A heat-sealing layer is optionally formed on the surface of the barrier resin coating layer or on the other side of the base film. Such barrier composite film has excellent transparency and retains high barrier properties and adhesive properties of covering layer despite its thin covering layer.