Abstract: A method including obtaining a metal pipe with a longitudinal submerged arc weld, an axis of the longitudinal submerged arc weld being oriented parallel to a rotationally symmetric axis of the metal pipe and cutting a first test beam and a second test beam from the metal pipe with each test beam extending on both sides of the axis of the longitudinal submerged arc weld and has a cuboid shape. The method further including forming a double-beam assembly by clamping two spacers between the first and second test beams such that the two spacers are symmetrically disposed at an equal distance on either side the longitudinal submerged arc weld. The method further including immersing the double-beam assembly in a liquid test solution for a predetermined period of time before removing it from the liquid test solution and disassembling the double-beam. The method further including examining the first and the second test beam using a metallographic sectioning method.

Abstract: A method including obtaining a metal pipe with a longitudinal submerged arc weld, an axis of the longitudinal submerged arc weld being oriented parallel to a rotationally symmetric axis of the metal pipe and cutting a first test beam and a second test beam from the metal pipe with each test beam extending on both sides of the axis of the longitudinal submerged arc weld and has a cuboid shape. The method further including forming a double-beam assembly by clamping two spacers between the first and second test beams such that the two spacers are symmetrically disposed at an equal distance on either side the longitudinal submerged arc weld. The method further including immersing the double-beam assembly in a liquid test solution for a predetermined period of time before removing it from the liquid test solution and disassembling the double-beam. The method further including examining the first and the second test beam using a metallographic sectioning method.

Abstract: A method of managing a tubular having a seam that exhibits signs of hydrogen induced cracking that extends radially along the seam, and which is different from classic step-wise cracking. Included in the method is evaluating the strength and ductility specimens taken from the tubular that have been hydrogen charged; and which provides an indication if the seam is susceptible to hydrogen embrittlement. The strength is evaluated by comparing tensile strength of the hydrogen charged specimen with that specified in an industry standard, such as API 5L. The ductility is evaluated based on comparing percent elongation of the hydrogen charged specimen with percent elongation of a specimen obtained from the tubular and not hydrogen charged. Tubulars with seams found susceptible to hydrogen embrittlement would not be put into sour service, whereas those found not susceptible to hydrogen embrittlement can be put in a sour service.

Abstract: A method of managing a tubular having a seam that exhibits signs of hydrogen induced cracking that extends radially along the seam, and which is different from classic step-wise cracking. Included in the method is evaluating the strength and ductility specimens taken from the tubular that have been hydrogen charged; and which provides an indication if the seam is susceptible to hydrogen embrittlement. The strength is evaluated by comparing tensile strength of the hydrogen charged specimen with that specified in an industry standard, such as API 5L. The ductility is evaluated based on comparing percent elongation of the hydrogen charged specimen with percent elongation of a specimen obtained from the tubular and not hydrogen charged. Tubulars with seams found susceptible to hydrogen embrittlement would not be put into sour service, whereas those found not susceptible to hydrogen embrittlement can be put in a sour service.