Abstract: Nanodispersions of inorganic clays in isocyanate may be created via pre-exfoliation, delamination, or both of the clay and subsequent mixing with isocyanate. In an embodiment, such an isocyanate nanodispersion is reacted with an isocyanate-reactive material or substrate to form a polyurethane nanocomposite.

Abstract: An embodiment of a closed-cell polymeric rigid foam may be made using a one-shot method and a reaction system that includes a hydrofluoroalkene physical blowing agent and a polyol mixture having an aminic polyol. The hydrofluoroalkene blowing agent has 3 to 5 carbon atoms and a boiling point between 10° C. and 40° C. at 1 atmosphere pressure. Embodiments of rigid foams may have high closed cell content and are particularly well suited for thermal insulation.

Abstract: An embodiment of a closed-cell polymeric rigid foam may be made using a one-shot method and a reaction system that includes a hydrofluoroalkene physical blowing agent and a polyol mixture having an aminic polyol. The hydrofluoroalkene blowing agent has 3 to 5 carbon atoms and a boiling point between 10° C. and 40° C. at 1 atmosphere pressure. Embodiments of rigid foams may have high closed cell content and are particularly well suited for thermal insulation.

Abstract: A blended material comprising (i) a binder composition comprising an isocyanate compound, a metallic catalyst, and an acid compound wherein the acid compound is present in the binder composition at an amount such that the acidity of the isocyanate compound ranges from 800 ppm to 10000 ppm, calculated as HCl; and (ii) a lignocellulosic material is disclosed. A lignocellulosic composite and a method of making such are also disclosed.

Abstract: An embodiment of a closed-cell polymeric rigid foam may be made using a one-shot method and a reaction system that includes a hydrofluoroalkene physical blowing agent and a polyol mixture having an aminic polyol. The hydrofluoroalkene blowing agent has 3 to 5 carbon atoms and a boiling point between 10° C. and 40° C. at 1 atmosphere pressure. Embodiments of rigid foams may have high closed cell content and are particularly well suited for thermal insulation.

Abstract: An embodiment of a closed-cell polymeric rigid foam may be made using a one-shot method and a reaction system that includes a hydrofluoroalkene physical blowing agent and a polyol mixture having an aminic polyol. The hydrofluoroalkene blowing agent has 3 to 5 carbon atoms and a boiling point between 10° C. and 40° C. at 1 atmosphere pressure. Embodiments of rigid foams may have high closed cell content and are particularly well suited for thermal insulation.

Abstract: Nanodispersions of inorganic clays in isocyanate may be created via pre-exfoliation, delamination, or both of the clay and subsequent mixing with isocyanate. In an embodiment, such an isocyanate nanodispersion is reacted with an isocyanate-reactive material or substrate to form a polyurethane nanocomposite.

Abstract: Improved low density polyurethane foams are prepared from an isocyanate-terminated prepolymer having an NCO content of more than about 31 to about 33.5% by weight comprising:(a) a polyphenylene polymethylene polyisocyanate comprising(i) about 30 to about 100% by weight of diphenylmethane diisocyanate and(ii) the remainder selected from the group consisting essentially of higher homologues of polyphenylene polymethylene polyisocyanate, isocyanate-containing ester groups, urea groups, biuret groups, aliphatic groups, carbodiimide groups, isocyanurate groups, uretdione groups and urethane groups; and(b) a polyoxyalkylene polyol having an oxyethylene content of about 30 to about 90%, a molecular weight of about 1000 to about 12000 and a functionality of about 2 to about 8.