Abstract: A carbon fiber bundle for resin reinforcement, wherein there are adhered by 0.1-5.0 mass % to a carbon fiber bundle in which multiple lengths of filament are bundled, a mixture created by mixing an organic polymer (A) having a mass-average molecular weight of 10000 or more and an organic compound (B) the thermal reduction rate specified in claim 1 of which is 5 mass % or more or an organic compound (B) the thermal reduction rate specified in claim 2 of which is 0.8 mass % or more, the amount of the organic polymer (A) adhered being 0.1 mass % or more.

Abstract: A fiber-reinforced thermoplastic resin prepreg containing (A) reinforcing fibers, (B) a sizing agent and (C) a polyamide resin is described, wherein the sizing agent (B) and the polyamide resin (C) satisfy the condition Nm/N0<4.0, wherein N0 is the average of torques necessary for maintaining the number of revolutions of a roller type blade at 100 rpm/15 minutes.

Abstract: The photosensitive resin composition of the present invention contains a vinyl-based (co)polymer (I) obtained by polymerizing a monomer mixture (?) containing a vinyl-based monomer (a) having a phenolic hydroxyl group, a vinyl-based copolymer (II) having a weight-average molecular weight of 15,000 to 120,000, obtained by polymerizing a monomer mixture (?) containing a vinyl-based monomer (b) represented by CH2?CR1COO(R2O)kR3 (wherein R1=a hydrogen atom or a methyl group, R2=a hydrocarbon group having a carbon number of 1 to 4, R3=a hydrogen atom or a methyl group, and k=1 to 90) and a carboxyl group-containing vinyl-based monomer (c), a photosensitive substance (III), and a compound (IV) which is a specific aromatic polyhydroxy compound.

Abstract: Provided are a carbon fibre thermoplastic resin prepreg which is a carbon fibre prepreg obtained by impregnating a PAN-based carbon fibre in which the average fibre fineness of a single fibre is 1.0 dtex to 2.4 dtex with a thermoplastic resin, wherein the thermoplastic resin satisfies 20?(FM/FS)?40 (where FM: flexural modulus (MPa) of a resin sheet comprising only the thermoplastic resin, and FS: flexural strength (MPa) of the resin sheet), a method for manufacturing the same, and a carbon fibre composite material employing the carbon fibre prepreg.