Abstract: An object of the present invention is to provide a copper foil excellent in softening resistance performance which reduces decrease in tensile strength after heat treatment at about 350° C. to 400° C. In order to achieve the object, a surface-treated copper foil provided with a rust-proofing treatment layer on both surfaces of a copper foil in which a rust-proofing treatment layer is constituted by zinc alloy, and the either rust-proofing treatment layer is a zinc alloy layer having zinc amount of 20 mg/m2 to 1,000 mg/m2; and the copper foil contains one or two or more of small amount elements selected from carbon, sulfur, chlorine and nitrogen, and a sum amount thereof is 100 ppm or more is adopted.

Abstract: In manufacturing of a negative electrode material of a lithium ion secondary battery provided with a negative electrode mixture layer including a negative electrode active substance on a surface of a negative electrode current collector, one or mixture selected from granular materials alloyable with lithium and carbon materials for storing and releasing lithium is used as the negative electrode active substance; manufacturing method of a negative electrode material for a lithium ion secondary battery employed is characterized in that an electro-deposited copper foil in which a surface roughness (Ra) is 0.20 ?m<Ra<0.50 ?m and the surface roughness (Ra) satisfies [0.053×D50(c)] ?m to [0.210×D50(c)] ?m where (D50(c)) is an average particle size of the negative electrode active substance is selectively used as the negative electrode current collector; a silane coupling agent treatment layer is provided on a surface of the electro-deposited copper foil.

Abstract: It is an object of the present invention to provide an electrodeposited copper foil which has a lower profile and a higher gloss than low-profile electrodeposited copper foil conventionally supplied in markets. For achieving this object, the present invention employs an electrodeposited copper foil which has a super low profile, the surface roughness (Rzjis) of the deposit side of lower than 1.0-micron meter, and the gloss [Gs(60-deg.)] thereof of not lower than 400 irrespective to its thickness. The present invention also provides a manufacturing method of an electrodeposited copper foil obtained by electrodeposition using a sulfuric acid base copper electrolytic solution obtained by adding 3-mercapto-1-propanesulfonic acid and/or bis(3-sulfopropyl)disulfide, a quaternary ammonium salt polymer having a cyclic structure, and chlorine.

Abstract: An object of the present invention is to eliminate deviation in the quality of a chromate film provided on a copper foil for a negative electrode current collector to eliminate fluctuation of electric capacity in a lithium ion secondary battery. To achieve the object, as the copper foil for a negative electrode current collector of a lithium ion secondary battery, a copper foil provided with a chromate film for a negative electrode current collector in which Cr(OH)3 constitutes 85 area % or more of the chromate film is employed. Further, the copper foil provided with a chromate film for a negative electrode current collector according to the present application is preferable to be that the apparent orientation number N of oxygen closest to chrome in the chromate film is 4.5 or more.

Abstract: It is an object to provide a surface-treated electro-deposited copper foil which has a low profile at a level equal to or excellent than that of low-profile surface-treated electro-deposited copper foils that have conventionally been supplied to the market and in which waviness affecting the straight line performance of wiring is small, and a method for manufacturing the same. In order to achieve this object, in the surface-treated electro-deposited copper foil, the maximum waviness height (Wmax) of the bonding surface to be bonded with an insulation layer-constituting material to be 0.05 ?m to 0.7 ?m, the maximum peak to valley height (PV) to be 0.05 to 1.5 ?m, and the surface roughness (Rzjis) to be 0.1 ?m to 1.0 ?m.

Abstract: An object of the present invention is to provide a method for manufacturing a copper foil for a negative electrode current collector (specifically, copper foil for a negative electrode current collector of a lithium ion secondary battery) more excellent in discoloration resistance to improve charge/discharge cycle life of a secondary battery. To achieve the object, a method for manufacturing a copper foil for a negative electrode current collector of a secondary battery subjecting the copper foil to rust-proofing treatment, the method characterized in that the copper foil is rust-proofing treated with a chromate-treatment solution having pH in the range from 3.5 to 7.0 to form a chromate film on the surface of the copper foil is employed.

Abstract: An object of the present invention is to provide a copper foil excellent in softening resistance performance which reduces decrease in tensile strength after heat treatment at about 350° C. to 400° C. In order to achieve the object, a surface-treated copper foil provided with a rust-proofing treatment layer on both surfaces of a copper foil in which a rust-proofing treatment layer is constituted by zinc, and the either rust-proofing treatment layer is a zinc layer having zinc amount of 20 mg/m2 to 1,000 mg/m2; and the copper foil contains one or two or more of small amount elements selected from carbon, sulfur, chlorine and nitrogen, and a sum amount thereof is 100 ppm or more is adopted.

Abstract: An object of the present invention is to provide a copper foil excellent in softening resistance performance which reduces decrease in tensile strength after heat treatment at about 350° C. to 400° C. In order to achieve the object, a surface-treated copper foil provided with a rust-proofing treatment layer on both surfaces of a copper foil in which a rust-proofing treatment layer is constituted by zinc alloy, and the either rust-proofing treatment layer is a zinc alloy layer having zinc amount of 20 mg/m2 to 1,000 mg/m2; and the copper foil contains one or two or more of small amount elements selected from carbon, sulfur, chlorine and nitrogen, and a sum amount thereof is 100 ppm or more is adopted.

Abstract: A copper foil for a negative electrode current collector of a lithium ion secondary battery enables prevention of deformation of the current collector even if the charge/discharge operation is repeatedly carried out. In a copper foil for a negative electrode current collector of a lithium ion secondary battery, a 10 mm wide test specimen composed of the copper foil is subjected to a tensile test, a maximum strain loaded on the copper foil is 30 N or higher in a region where “Value L” represented by the following expression is 0.

Abstract: An object of the present invention is to provide a method for preparing a sulfuric acid base copper electrolytic solution used for formation of an electro-deposited copper film comprising a surface excellent in smoothness and gloss when formed by using the solution just after preparation and is prepared by using mono-sulfides. To achieve the object, a sulfuric acid base copper electrolytic solution is made to contain a sulfonated active sulfur compound, the bis(3-sulfopropyl)disulfide which is recommended for formation of a glossy electro-deposited copper film. And the bis(3-sulfopropyl)disulfide contained is obtained by converting a 3-mercapto-1-propanesulfonic acid into the bis(3-sulfopropyl)disulfide in an aqueous solution of the 3-mercapto-1-propanesulfonic acid by an oxidation reaction. In the oxidation reaction, an air bubbling method is preferably used to prevent oxidative decomposition of the 3-mercapto-1-propanesulfonic acid.

Abstract: An object of the present invention is to provide a method for preparing a sulfuric acid base copper electrolytic solution used for formation of an electro-deposited copper film comprising a surface excellent in smoothness and gloss when formed by using the solution just after preparation and is prepared by using mono-sulfides. To achieve the object, a sulfuric acid base copper electrolytic solution is made to contain a sulfonated active sulfur compound, the bis(3-sulfopropyl)disulfide which is recommended for formation of a glossy electro-deposited copper film. And the bis(3-sulfopropyl)disulfide contained is obtained by converting a 3-mercapto-1-propanesulfonic acid into the bis(3-sulfopropyl)disulfide in an aqueous solution of the 3-mercapto-1-propanesulfonic acid by an oxidation reaction. In the oxidation reaction, an air bubbling method is preferably used to prevent oxidative decomposition of the 3-mercapto-1-propanesulfonic acid.

Abstract: An object of the present invention is to provide a production method which enables efficient production of an electro-deposited copper foil with further lower profile when compared to the low-profile electro-deposited copper foils which have been supplied to the market and is excellent in mechanical strength. For the purpose of achieving the object, a production method adopted obtains the electro-deposited copper foil by electrolyzing a sulfuric acid based copper electrolytic solution which contains a quaternary ammonium salt polymer having cyclic structure and chlorine, wherein for the quaternary ammonium salt polymer contained in the sulfuric acid based copper electrolytic solution, a DDAC dimer or higher polymer is used. For the quaternary ammonium salt polymer, a diallyl dimethyl ammonium chloride polymer having a number average molecular weight of 300 to 10000 is preferably used.

Abstract: It is an object to provide a surface-treated electro-deposited copper foil which has a low profile at a level equal to or excellent than that of low-profile surface-treated electro-deposited copper foils that have conventionally been supplied to the market and in which waviness affecting the straight line performance of wiring is small, and a method for manufacturing the same. In order to achieve this object, in the surface-treated electro-deposited copper foil, the maximum waviness height (Wmax) of the bonding surface to be bonded with an insulation layer-constituting material to be 0.05 ?m to 0.7 ?m, the maximum peak to valley height (PV) to be 0.05 to 1.5 ?m, and the surface roughness (Rzjis) to be 0.1 ?m to 1.0 ?m.

Abstract: The purpose is to provide a cathode electrode for manufacturing an electrodeposited copper foil which is possible to be continuously and stably usable for a long duration of 3000 hours or longer to subsequently lessen the frequency of maintenance work execution as low as possible and to contribute to lower the running cost of the electrodeposited copper foil manufacture. As the means for achieving the purpose, a cathode electrode made of a titanium material is employed for obtaining an electrodeposited copper foil using an electrolytic copper solution and the titanium material having 7.0 or higher crystal grain size number and 35 ppm or lower initial hydrogen content is used for manufacturing the cathode electrode for manufacturing an electrodeposited copper foil. Further, also provided is a manufacturing method of the titanium material to be employed for the cathode electrode made of a titanium material.

Abstract: The purpose is to provide a cathode electrode for manufacturing an electrodeposited copper foil which is possible to be continuously and stably usable for a long duration of 3000 hours or longer to subsequently lessen the frequency of maintenance work execution as low as possible and to contribute to lower the running cost of the electrodeposited copper foil manufacture. As the means for achieving the purpose, a cathode electrode made of a titanium material is employed for obtaining an electrodeposited copper foil using an electrolytic copper solution and the titanium material having 7.0 or higher crystal grain size number and 35 ppm or lower initial hydrogen content is used for manufacturing the cathode electrode for manufacturing an electrodeposited copper foil. Further, also provided is a manufacturing method of the titanium material to be employed for the cathode electrode made of a titanium material.