Abstract: The present configuration relates to the use of a hanging bracket which may be assembled on a construction job site in order to allow such materials to be dispensed along with the use of typical onsite construction vehicles such as backhoes, bucket loaders, etc. This configuration allows for effective attachment to various bucket sizes, and also may be folded into a compact configuration when stored or transported.

Abstract: In some embodiments of the present invention a method includes: obtaining a first aluminum alloy sheet formed from rolling a first ingot of a 3xxx or a 5xxx series aluminum alloy, wherein, prior to rolling, the first ingot has been heated to a sufficient temperature for a sufficient time to achieve a first dispersoid f/r of less than 7.65; and forming a container precursor from the first aluminum alloy sheet, wherein when the first aluminum alloy sheet is formed into the container precursor, the container precursor has less observed surface striations and ridges as compared to a container precursor formed from a second aluminum alloy sheet rolled from a second ingot having a second dispersoid f/r value of 7.65 or greater.

Abstract: In some embodiments of the present invention a method includes: obtaining a first aluminum alloy sheet formed from rolling a first ingot of a 3xxx or a 5xxx series aluminum alloy, wherein, prior to rolling, the first ingot has been heated to a sufficient temperature for a sufficient time to achieve a first dispersoid f/r of less than 7.65; and forming a container precursor from the first aluminum alloy sheet, wherein when the first aluminum alloy sheet is formed into the container precursor, the container precursor has less observed surface striations and ridges as compared to a container precursor formed from a second aluminum alloy sheet rolled from a second ingot having a second dispersoid f/r value of 7.65 or greater.

Abstract: An aluminum sheet comprises a 3XXX or a 5xxx alloy having a tensile yield strength as measured in the longitudinal direction of 27-33 ksi and an ultimate tensile strength; wherein the ultimate tensile strength minus the tensile yield strength is less than 3.30 ksi (UTS?TYS<3.30 ksi). An aluminum container has a dome, wherein the dome comprises a AA 3XXX or a 5xxx having a tensile yield strength as measured in the longitudinal direction of 27-33 ksi and an ultimate tensile strength; wherein the ultimate tensile strength minus the tensile yield strength is less than 3.30 ksi (UTS?TYS<3.30 ksi).