Abstract: In A dispersion of graphenic carbon nanoparticles is disclosed comprising a solvent, greater than one weight percent graphenic carbon nanoparticles based upon a total weight of the dispersion comprising thermally produced graphenic carbon nanoparticles and base graphene particles, and a polymeric resin dispersant. The weight ratio of the graphenic carbon nanoparticles to the dispersant may be greater than 5:1, and the dispersion may have an instability index of less than 0.7. A method is also disclosed for dispersing graphenic carbon particles in a solvent. A polymeric resin dispersant is mixed into the solvent, and graphenic carbon nanoparticles comprising thermally produced graphenic carbon nanoparticles and base graphenic particles are dispersed into the solvent.

Abstract: The present invention is directed to an aqueous curable film-forming composition comprising: (a) a film-forming component comprising an aliphatic di- or higher functional polyisocyanate; and (b) a catalyst additive comprising: (i) a catalytic organic compound comprising iron (II) and optionally tin; and (ii) a beta-diketone. The present invention is further directed to a method of controlling the rate of cure of an aqueous curable film-forming composition. The method comprises adding to the aqueous curable film-forming composition the catalyst additive described above; the aqueous curable film-forming composition comprises a film-forming component comprising an aliphatic di- or higher functional polyisocyanate. The present invention is additionally directed to a coated article comprising a cured coating layer applied on at least one surface of a substrate to form a coated substrate; wherein the cured coating layer is deposited from the aqueous curable film-forming composition described above.