Abstract: Disclosed herein is a method of preparing a rotating member to enhance bearing durability comprising, applying a metal material to a surface of the rotor orthogonal to a longitudinal axis of the rotor, the material having a chromium content less than a chromium content of the rotating member, and surfacing said metal material orthogonal to the axis of the rotor. Further disclosed herein is an enhanced bearing durability rotating member comprising, a rotor with a metal material surface orthogonal to a longitudinal axis of the rotor having less chromium content than the rotor, and a boundary layer between the metal material surface and the rotor orthogonal to the axis of the rotor.

Abstract: A method for welding two sections of a rotor together, wherein each rotor section includes a welding surface, is provided. The method includes positioning the welding surface of the first rotor section substantially flush against the welding surface of the second rotor section. The method also includes positioning the second section substantially flush against a flange circumscribing the first section such that a rabbeted joint is defined therebetween.

Abstract: A method for heat treating a serviced turbine part to improve a hold time fatigue cracking resistance of the serviced turbine part is provided. The method includes positioning the serviced turbine part in a vacuum furnace configured to limit surface oxidation. The serviced turbine part is controllably heated to prevent distortion. A surface damage layer is recrystallized into a fine grain structure to prevent fatigue crack initiation. The serviced turbine part is controllably cooled to prevent distortion.

Abstract: A method of heat treating a turbine rotor disk to obtain different radial properties at different locations in the rotor disk includes a) heating the rotor disk for a period of from 4 to 10 hours at a temperature of 1800° F.; b) cooling the rotor disk to a temperature of about 1550° F.; c) holding the rotor disk at about 1550° F. for a period of from about 2 to about 4 hours; d) cooling the rotor disk to room temperature; e) precipitation aging the rotor disk by heating the rotor disk to temperature of 1325° F. for 8 hours, holding it at 1150° F. for 8 hours, and f) cooling the rotor disk.

Abstract: Disclosed herein is a turbine component comprising a substrate; and a protective structure formed on the substrate, wherein the protective structure comprises an ?-? titanium alloy, a ?-titanium alloy or a near-? titanium alloy. Disclosed herein too is a process for providing a protective structure to a turbine component, comprising affixing a protective structure on a turbine component; wherein the protective structure comprises an ?-? titanium alloy, a near-? titanium alloy or a ?-titanium alloy.