Abstract: A method for tuning characteristics of a polyamide nanofiber nonwoven comprising the step of targeting a specific average nanofiber diameter and/or a specific relative viscosity for the polyamide nanofiber nonwoven. The specific average nanofiber diameter is within a range from 100 nm to 1000 nm and/or the specific relative viscosity is within a range from 5 to 75, e.g., from 15 to 50. The process further comprises the steps of extruding a polyamide composition having a moisture content with a pressurized gas through a fiber forming channel having a channel temperature to form the polyamide nanofiber nonwoven having the target average nanofiber diameter and/or relative viscosity and controlling the moisture content, the pressure of pressurized gas, and/or the channel temperature based on the specific average nanofiber diameter and/or the specific relative viscosity.

Abstract: The present disclosure relates to a nonwoven polyamide structure having antimicrobial properties comprising: nonwoven polyamide fibers comprising less than 4000 ppm zinc dispersed within the nonwoven polyamide fibers; and less than 2000 ppm phosphorus. The fibers have an average fiber diameter of less than 25 microns; and the polyamide structure demonstrates a Staphylococcus aureus reduction of at least 90%, as measured by ISO 20743-13.

Abstract: The present disclosure relates to a nonwoven polyamide structure having antimicrobial properties comprising: nonwoven polyamide fibers comprising less than 4000 ppm zinc dispersed within the nonwoven polyamide fibers; and less than 2000 ppm phosphorus. The fibers have an average fiber diameter of less than 25 microns; and the polyamide structure demonstrates a Staphylococcus Aureus reduction of at least 90%, as measured by ISO 20743-13.

Abstract: A nanofiber nonwoven product is disclosed which comprises a polyamide with a relative viscosity from 2 to 330, spun into nanofibers with an average diameter of less than 1000 nanometers (1 micron). In general, the inventive products are prepared by: (a) providing a polyamide composition, wherein the polyamide has a relative viscosity from 2 to 330; (b) melt spinning the polyamide composition into a plurality of nanofibers having an average fiber diameter of less than 1 micron, followed by (c) forming the nanofibers into the product.

Abstract: The present disclosure relates to polymer resins, fibers, and yarns with permanent antimicrobial activity, and a method of producing the same. In one embodiment, the antimicrobial polymer resin comprises a polymer having less than 2500 ppm of zinc dispersed within the polymer, less than 1000 ppm of phosphorus, wherein the weight ratio of zinc to phosphorus is at least 1.3:1 or less than 0.64:1.

Abstract: A nanofiber nonwoven product is disclosed which comprises a polyamide with a relative viscosity from 2 to 330, spun into nanofibers with an average diameter of less than 1000 nanometers (1 micron). In general, the inventive products are prepared by: (a) providing a polyamide composition, wherein the polyamide has a relative viscosity from 2 to 330; (b) melt spinning the polyamide composition into a plurality of nanofibers having an average fiber diameter of less than 1 micron, followed by (c) forming the nanofibers into the product.

Abstract: A nanofiber nonwoven product is disclosed which comprises a polyamide with a relative viscosity from 2 to 330, spun into nanofibers with an average diameter of less than 1000 nanometers (1 micron). In general, the inventive products are prepared by: (a) providing a polyamide composition, wherein the polyamide has a relative viscosity from 2 to 330; (b) melt spinning the polyamide composition into a plurality of nanofibers having an average fiber diameter of less than 1 micron, followed by (c) forming the nanofibers into the product.

Abstract: The present disclosure relates to polymer resins, fibers, and yarns with permanent antimicrobial activity, and a method of producing the same. In one embodiment, the antimicrobial polymer resin comprises a polymer having less than 2500 ppm of zinc dispersed within the polymer, less than 1000 ppm of phosphorus, wherein the weight ratio of zinc to phosphorus is at least 1.3:1 or less than 0.64:1.

Abstract: A nanofiber nonwoven product is disclosed which comprises a polyamide with a relative viscosity from 2 to 330, spun into nanofibers with an average diameter of less than 1000 nanometers (1 micron). In general, the inventive products are prepared by: (a) providing a polyamide composition, wherein the polyamide has a relative viscosity from 2 to 330; (b) melt spinning the polyamide composition into a plurality of nanofibers having an average fiber diameter of less than 1 micron, followed by (c) forming the nanofibers into the product.

Abstract: A filter comprising a nanofiber nonwoven product is disclosed which comprises a polyamide with a relative viscosity from 2 to 330, spun into nanofibers with an average diameter of less than 1000 nanometers (1 micron). In general, the inventive products are prepared by: (a) providing a polyamide composition, wherein the polyamide has a relative viscosity from 2 to 330; (b) melt spinning the polyamide composition into a plurality of nanofibers having an average fiber diameter of less than 1 micron, followed by (c) forming the nanofibers into the product.

Abstract: The present disclosure relates the polymer compositions, fibers, and yarns having near-permanent antimicrobial activity, and a method of producing the same. In one embodiment, the antimicrobial polymer composition from 50 wt % to 99.9 wt % of a polymer, from 5 wppm to 1000 wppm of zinc, and from 0.005 wt % to 1 wt % of phosphorus, wherein fibers formed from the polymer composition demonstrate a zinc retention rate of greater than 20% when tested in a dye bath test.

Abstract: The present disclosure relates the polymer compositions, fibers, and yarns having near-permanent antimicrobial activity, and a method of producing the same. In one embodiment, the antimicrobial polymer composition from 50 wt % to 99.9 wt % of a polymer, from 5 wppm to 1000 wppm of zinc, and from 0.005 wt % to 1 wt % of phosphorus, wherein fibers formed from the polymer composition demonstrate a zinc retention rate of greater than 20% when tested in a dye bath test.

Abstract: A method for tuning characteristics of a polyamide nanofiber nonwoven comprising the step of targeting a specific average nanofiber diameter and/or a specific relative viscosity for the polyamide nanofiber nonwoven. The specific average nanofiber diameter is within a range from 100 nm to 1000 nm and/or the specific relative viscosity is within a range from 5 to 75, e.g., from 15 to 50. The process further comprises the steps of extruding a polyamide composition having a moisture content with a pressurized gas through a fiber forming channel having a channel temperature to form the polyamide nanofiber nonwoven having the target average nanofiber diameter and/or relative viscosity and controlling the moisture content, the pressure of pressurized gas, and/or the channel temperature based on the specific average nanofiber diameter and/or the specific relative viscosity.

Abstract: A method for tuning characteristics of a polyamide nanofiber nonwoven comprising the step of targeting a specific average nanofiber diameter and/or a specific relative viscosity for the polyamide nanofiber nonwoven. The specific average nanofiber diameter is within a range from 100 nm to 1000 nm and/or the specific relative viscosity is within a range from 5 to 75, e.g., from 15 to 50. The process further comprises the steps of extruding a polyamide composition having a moisture content with a pressurized gas through a fiber forming channel having a channel temperature to form the polyamide nanofiber nonwoven having the target average nanofiber diameter and/or relative viscosity and controlling the moisture content, the pressure of pressurized gas, and/or the channel temperature based on the specific average nanofiber diameter and/or the specific relative viscosity.

Abstract: A nanofiber nonwoven product is disclosed which comprises a polyamide with a relative viscosity from 2 to 330, spun into nanofibers with an average diameter of less than 1000 nanometers (1 micron). In general, the inventive products are prepared by: (a) providing a polyamide composition, wherein the polyamide has a relative viscosity from 2 to 330; (b) melt spinning the polyamide composition into a plurality of nanofibers having an average fiber diameter of less than 1 micron, followed by (c) forming the nanofibers into the product.

Abstract: The present disclosure relates to a process for preparing fibers and/or fabrics having antimicrobial properties, the process comprising: determining an operating pressure limit; calculating an amount of zinc based on the operating pressure limit; forming a polyamide composition comprising: polyamide; and the calculated amount of zinc; forming fibers from the polyamide composition, wherein the forming is conducted at an operating pressure below the operating pressure limit.

Abstract: A nanofiber nonwoven product is disclosed which comprises a polyamide with a relative viscosity from 2 to 330, spun into nanofibers with an average diameter of less than 1000 nanometers (1 micron). In general, the inventive products are prepared by: (a) providing a polyamide composition, wherein the polyamide has a relative viscosity from 2 to 330; (b) melt spinning the polyamide composition into a plurality of nanofibers having an average fiber diameter of less than 1 micron, followed by (c) forming the nanofibers into the product.

Abstract: A filter comprising a nanofiber nonwoven product is disclosed which comprises a polyamide with a relative viscosity from 2 to 330, spun into nanofibers with an average diameter of less than 1000 nanometers (1 micron). In general, the inventive products are prepared by: (a) providing a polyamide composition, wherein the polyamide has a relative viscosity from 2 to 330; (b) melt spinning the polyamide composition into a plurality of nanofibers having an average fiber diameter of less than 1 micron, followed by (c) forming the nanofibers into the product.

Abstract: The present disclosure relates the polymer compositions, fibers, and yarns having near-permanent antimicrobial activity, and a method of producing the same. In one embodiment, the antimicrobial polymer composition from 50 wt % to 99.9 wt % of a polymer, from 5 wppm to 1000 wppm of zinc, and from 0.005 wt % to 1 wt % of phosphorus, wherein fibers formed from the polymer composition demonstrate a zinc retention rate of greater than 20% when tested in a dye bath test.

Abstract: The present disclosure relates to a nonwoven polyamide structure having antimicrobial properties comprising: nonwoven polyamide fibers comprising less than 4000 ppm zinc dispersed within the nonwoven polyamide fibers; and less than 2000 ppm phosphorus. The fibers have an average fiber diameter of less than 25 microns; and the polyamide structure demonstrates a Staphylococcus Aureus reduction of at least 90%, as measured by ISO 20743-13.