Patents by Inventor Se Gu Son

Se Gu Son has filed for patents to protect the following inventions. This listing includes patent applications that are pending as well as patents that have already been granted by the United States Patent and Trademark Office (USPTO).

  • Patent number: 7682448
    Abstract: A high compressive strength silica mortar to be used for the installation of constructs such as building inside and outside walls, the road pavement, a slope and planting trees in the roof and manufacturing method thereof are provided. The high compressive strength silica mortar is formed of 30 to 60 wt % of silica, 40 to 70 wt % of blast furnace slag, and the 15 to 35 weight parts of polycondensation regulator for 100 weight parts of dry mortar powder of these silica and blast furnace slag, and is solidified by generating C—S—H, C-A-H, amorphous Geopolymeric Matrix{Al2O3.mSiO2.nM2O.xH2O(M=K,Na,Ca)} and Zeolite in the mortar. In particular, the high compressive strength silica mortar exhibits the compressive strength of 70.0 MPa or more by vibration forming and curing for 12˜48 hours at 25 to 80° C. before removal of form and aging for 28 days, and can save energies because a firing process is not required.
    Type: Grant
    Filed: March 26, 2008
    Date of Patent: March 23, 2010
    Assignees: Yeram Communication Co., Ltd
    Inventors: Young Do Kim, Se Gu Son, Seung Yeob Hong, Soo Bok Jeong
  • Publication number: 20090229493
    Abstract: A high compressive strength silica mortar to be used for the installation of constructs such as building inside and outside walls, the road pavement, a slope and planting trees in the roof and manufacturing method thereof are provided. The high compressive strength silica mortar is formed of 30 to 70 wt % of silica, 40 to 70 wt % of blast furnace slag, and the 15 to 35 weight parts of polycondensation regulator for 100 weight parts of dry mortar powder of these silica and blast furnace slag, and is solidified by generating C—S—H, C-A-H, amorphous Geopolymeric Matrix {Al2O3.mSiO2.nM2O.xH2O(M=K,Na,Ca)} and Zeolite in the mortar. In particular, the high compressive strength silica mortar exhibits the compressive strength of 70.0 MPa or more by vibration forming and curing for 12˜48 hours at 25 to 80° C. before removal of form and aging for 28 days, and can save energies because a firing process is not required.
    Type: Application
    Filed: March 26, 2008
    Publication date: September 17, 2009
    Inventors: Young Do KIM, Se Gu SON, Seung Yeob HONG, Soo Bok JEONG