Abstract: In a method for producing a cold-rolled steel sheet by continuously casting, hot-rolling, cold-rolling, and continuously annealing Al-killed steel, it is known to coil a hot-rolled strip at a coiling temperature of 630.degree. C. to 710.degree. C. so as to attain satisfactory precipitation of AlN in the hot-rolling step. When the direct-rolling of a continuously cast strand (DR method) is employed to produce a cold-rolled strip, it is impossible to attain satisfactory precipitation of AlN even by carrying out the known coiling method. The present invention is characterized in that an extremely high coiling temperature of at least 780.degree. C. is used to essentially prevent aging due to the precipitation of AlN, and, further, the carbon content of a continuously cast slab is 0.005% at the highest so as to essentially prevent the occurrence of orange peel. Heat conservation due to use of the DR method and excellent properties of the cold-rolled steel strip are simultaneously attained.