Abstract: The resin composition for a platable substrate of the present invention comprises 100 parts by weight of a resin composition (C) comprising 10 to 60% by weight of a graft copolymer (A) prepared by graft polymerization of a rubbery polymer (A1) and a monomer component (A2) containing an aromatic alkenyl compound monomer unit (a) and a vinyl cyanide compound monomer unit (b) and 40 to 90% by weight of the other polymer (B) (provided that the total amount of the components (A) and (B) is 100% by weight), and 5 to 40 parts by weight of a phosphate ester flame retardant (D) having a molecular weight of more than 326 or 2 to 40 parts by weight of a red phosphorus flame retardant (D?). The resin composition for a platable substrate of the present invention is excellent in production stability such as moldability, dimensional stability, mechanical strength and plating properties, and is also environmentally friendly.

Abstract: The resin composition for a platable substrate of the present invention comprises 100 parts by weight of a resin composition (C) comprising 10 to 60% by weight of a graft copolymer (A) prepared by graft polymerization of a rubbery polymer (A1) and a monomer component (A2) containing an aromatic alkenyl compound monomer unit (a) and a vinyl cyanide compound monomer unit (b) and 40 to 90% by weight of the other polymer (B) (provided that the total amount of the components (A) and (B) is 100% by weight), and 5 to 40 parts by weight of a phosphate ester flame retardant (D) having a molecular weight of more than 326 or 2 to 40 parts by weight of a red phosphorus flame retardant (D′). The resin composition for a platable substrate of the present invention is excellent in production stability such as moldability, dimensional stability, mechanical strength and plating properties, and is also environmentally friendly.

Abstract: A maleimide-based copolymer containing maleimide monomer units (a-1), aromatic vinyl monomer units (a-2) and other vinyl monomer units (a-3), wherein,(I) the content of residual maleimide monomer in the copolymer is 0.1% by weight or less, and the content of whole volatiles other than the maleimide monomer is 0.5% by weight or less;(II) a compound obtained from at least one monomer selected from the group consisting of a maleimide monomer, an aromatic vinyl monomer and other vinyl monomers, having a weight-average molecular weight of from 200 to 1,000, is contained in an amount of 2 to 10% by weight;(III) the copolymer has a yellow index of 30 or less; and(IV) the copolymer has an intrinsic viscosity of from 0.3 to 1.5.

Abstract: A resin composition, excellent in a physical property balance between chemical resistance and impact strength, obtained by mixing at least one graft copolymer selected from the group consisting of a graft copolymer in which a copolymer rubber of an alkyl acrylate and a conjugated diene is used, a graft copolymer in which a rubber prepared by seed rubber polymerizing an alkyl acrylate with a conjugated diene rubber is used and a graft copolymer in which a rubber prepared by seed rubber polymerizing an alkyl acrylate with a polyorganosiloxane rubber is used, with a graft copolymer in which a conjugated diene rubber is used, and optionally with a rigid thermoplastic resin.

Abstract: A resin composition, excellent in a physical property balance between chemical resistance and impact strength, obtained by mixing at least one graft copolymer selected from the group consisting of a graft copolymer in which a copolymer rubber of an alkyl acrylate and a conjugated diene is used, a graft copolymer in which a rubber prepared by seed rubber polymerizing an alkyl acrylate with a conjugated diene rubber is used and a graft copolymer in which a rubber prepared by seed rubber polymerizing an alkyl acrylate with a polyorganosiloxane rubber is used, with a graft copolymer in which a conjugated diene rubber is used, and optionally with a rigid thermoplastic resin.

Abstract: Disclosed is an impact-resistant thermoplastic resin composition comprising (a) a graft copolymer (II) prepared by polymerizing a monomer or monomer mixture predominantly comprised of methyl methacrylate and/or styrene in the presence of an agglomerated rubber copolymer (I') latex, and (b) bent-resistant rigid thermoplastic resin (III) comprised of .alpha.-methylstyrene or a maleimide compound. The agglomerated rubber copolymer (I') is prepared by emulsion-polymerizing an alkyl acrylate/1,3-butadiene mixture, and then agglomerating the resulting rubbery copolymer. The agglomeration is effected by adding (a) an acid group-containing copolymer prepared by emulsion polymerizing an alkyl methacrylate/unsaturated monomer mixture, and/or (b) an oxy acid salt selected from alkali metal, alkaline earth metal, zinc, nickel and aluminum salts of oxy acids having as the center element an element selected from elements belonging to the second and third periods of groups IIIA through VIA of the Periodic Table.