Abstract: Provided is a method of preparing a polymer polyol, including steps of: (a) polymerizing a polyol and a monomer in presence of a diluent to prepare a primary particle dispersed liquid; and (b) feeding an additional polyol and monomer into the primary particle dispersed liquid and polymerizing to prepare a secondary particle dispersed liquid.

Abstract: Provided is a method of preparing a polymer polyol including steps of (a) respectively batchwise feeding a polyol and a monomer in a weight ratio of 40 to 60:40 to 60 into a reactor to prepare a mixture; and (b) polymerizing the mixture for 1 to 5 hours to prepare monodispersed particles.

Abstract: Provided is a method of preparing a polymer polyol including steps of (a) respectively batchwise feeding a polyol and a monomer in a weight ratio of 40 to 60:40 to 60 into a reactor to prepare a mixture; and (b) polymerizing the mixture for 1 to 5 hours to prepare monodispersed particles.

Abstract: Provided is a method of preparing a polymer polyol, including steps of: (a) polymerizing a polyol and a monomer in presence of a diluent to prepare a primary particle dispersed liquid; and (b) feeding an additional polyol and monomer into the primary particle dispersed liquid and polymerizing to prepare a secondary particle dispersed liquid.

Abstract: Provided is a functional styrene-butadiene copolymer having superior silica affinity. The copolymer is prepared by radical polymerizing a styrene monomer, a butadiene monomer and a reactive polyol monomer in emulsion state in order to maximize the mixing effect when compounding with silica. When mixed with silica, the disclosed styrene-butadiene copolymer provides excellent wet traction and superior abrasion resistance, and is suitable to be used for an industrial material of snow tires, belts, hoses, etc.

Abstract: Provided is a functional styrene-butadiene copolymer having superior silica affinity. The copolymer is prepared by radical polymerizing a styrene monomer, a butadiene monomer and a reactive polyol monomer in emulsion state in order to maximize the mixing effect when compounding with silica. When mixed with silica, the disclosed styrene-butadiene copolymer provides excellent wet traction and superior abrasion resistance, and is suitable to be used for an industrial material of snow tires, belts, hoses, etc.

Abstract: Disclosed herein is a novel stabilizer for preparing a polymer polyol, which is used to prepare polyurethane foam having improved physical properties. The stabilizer is prepared by allowing maleic anhydride to react with a polyether polyol, having an OH functionality of 3-8 and a molecular weight of 3,000-15,000, and then adding ethylene oxide to the reaction solution. Because the molecular weight and functionality of the stabilizer are increased through aging and dimerization, the stabilizer has a high molecular weight of 5,000-30,000, a high OH functionality of 6-10 and a viscosity of 3,000-15,000 cps/25° C. A polymer polyol derived from the stabilizer has low viscosity compared to those of prior products and contributes to the improvement in the physical properties of the resulting polyurethane foam.

Abstract: Disclosed herein is a novel stabilizer for preparing a polymer polyol, which is used to prepare polyurethane foam having improved physical properties. The stabilizer is prepared by allowing maleic anhydride to react with a polyether polyol, having an OH functionality of 3-8 and a molecular weight of 3,000-15,000, and then adding ethylene oxide to the reaction solution. Because the molecular weight and functionality of the stabilizer are increased through aging and dimerization, the stabilizer has a high molecular weight of 5,000-30,000, a high OH functionality of 6-10 and a viscosity of 3,000-15,000 cps/25° C. A polymer polyol derived from the stabilizer has low viscosity compared to those of prior products and contributes to the improvement in the physical properties of the resulting polyurethane foam.