Abstract: Disclosed is a hot-stamping component, which includes a base steel plate; and a plated layer on the base steel plate and including a first layer, a second layer, and an intermetallic compound portion having an island shape in the second layer, wherein the first layer and the second layer are sequentially stacked, and an area fraction of the intermetallic compound portion with respect to the second layer is an amount of 20% to 60%.

Abstract: Disclosed is a hot-stamping component, which includes a base steel plate; and a plated layer on the base steel plate and including a first layer, a second layer, and an intermetallic compound portion having an island shape in the second layer, wherein the first layer and the second layer are sequentially stacked, and an area fraction of the intermetallic compound portion with respect to the second layer is an amount of 20% to 60%.

Abstract: Provided is a hot stamping component having a tensile strength of 1680 Mpa or greater including a microstructure comprising prior austenite grains (PAGs), and an average grain diameter of the PAGs is 25 ?m or less.

Abstract: One embodiment of the present invention discloses a member for automobile structure including a base steel sheet and a plating layer covering at least one surface of the base steel sheet, wherein the member for automobile structure has a tensile strength of 1350 MPa or greater and a yield strength of 900 MPa or greater, wherein the base steel sheet includes a martensite phase having an area fraction of 80% or greater, an iron-based carbide located inside the martensite phase and having an area fraction of less than 5% based on the martensite phase, and precipitates distributed inside the base steel sheet, wherein a mismatch dislocation exists at the interface between iron and the precipitates of the base steel sheet, and a difference between lattice constants of the iron and the precipitates is less than 25% of the lattice constants of the iron.

Abstract: The present invention provides a hot stamping component having a tensile strength of 1350 Mpa or greater, including a microstructure including prior austenite grains (PAG), wherein an average particle diameter of the PAGs is 35 ?m or less.

Abstract: Disclosed is a hot-stamping component, which includes a base steel plate; and a plated layer on the base steel plate and including a first layer, a second layer, and an intermetallic compound portion having an island shape in the second layer, wherein the first layer and the second layer are sequentially stacked, and an area fraction of the intermetallic compound portion with respect to the second layer is an amount of 20% to 60%.

Abstract: A method of manufacturing a hot stamping includes: inserting a blank having a plating layer formed on at least one surface of a base material into a heating furnace having a plurality of sections having different temperature increase rate ranges; and multi-stage heating the blank gradually while passing through the plurality of sections. The plurality of sections include: a first heating section having a first average temperature increase rate change rate; a second heating section having a second average temperature increase rate change rate different from the first average temperature increase rate change rate; and a third heating section having a third average temperature increase rate change rate different from the first average temperature increase rate change rate and the second average temperature increase rate change rate. The third average temperature increase rate change rate includes a section in which a positive value is changed to a negative value.

Abstract: According to an aspect of the present disclosure, provided is a method of manufacturing a hot stamping component in which a residual stress analysis value satisfies a preset condition. The method includes heating a blank; forming a molded body by hot stamping the blank; and cooling the molded body to form a hot stamped component. The residual stress analysis value may be a product of a magnitude of an X-ray diffraction analysis (XRD) value obtained by quantifying residual stress by XRD analysis and a magnitude of an electron backscatter diffraction (EBSD) value obtained by quantifying an orientation by EBSD analysis, and the preset condition is about 2.85* 10-4 Degree*MPa/µm2 or greater and about 0.05 Degree*MPa/µm2 or less.

Abstract: Disclosed is a method of manufacturing a blank for hot stamping, which includes forming a plated layer on a steel plate by immersing the steel plate in a plating bath including aluminum and silicon; and heating the steel plate on which the plated layer is formed at a first temperature for a first time period.

Abstract: Disclosed is a hot-stamping component, which includes a base steel plate; and a plated layer on the base steel plate and including a first layer, a second layer, and an intermetallic compound portion having an island shape in the second layer, wherein the first layer and the second layer are sequentially stacked, and an area fraction of the intermetallic compound portion with respect to the second layer is an amount of 20% to 60%.