Abstract: The present disclosure belongs to the field of battery materials, and discloses a coated nickel-rich ternary material and a preparation method and application thereof. The coated nickel-rich ternary material has a chemical formula of LiNixCoyMnzO2·a[M3(PO4)2·bH2O], Where 0.6?x?0.8, 0.1?y?0.2, 0.1?z?0.2, x+y+z=1, 0.01?a?0.03, 3?b?8, M3(PO4)2·bH2O is at least one selected from the group consisting of nickel phosphate, cobalt phosphate and manganese phosphate; the coated nickel-rich ternary material has a flower-like structure. The preparation method of the present disclosure provides phosphate ions through the prepared phosphate solution, performs coating in a liquid phase environment, and synthesizes the precursor simultaneously by microwave hydrothermal synthesis, which is beneficial to the full contact between the phosphates and the precursor, and ensures the surface of the nickel-rich ternary precursor is uniformly coated with the phosphates. The method is simple and has good coating effect.

Abstract: The present disclosure belongs to the field of battery materials, and discloses a coated nickel-rich ternary material and a preparation method and application thereof. The coated nickel-rich ternary material has a chemical formula of LiNixCoyMnzO2·a[M3(PO4)2·bH2O], Where 0.6?x?0.8, 0.1?y?0.2, 0.1?z?0.2, x+y+z=1, 0.01?a?0.03, 3?b?8, M3(PO4)2·bH2O is at least one selected from the group consisting of nickel phosphate, cobalt phosphate and manganese phosphate; the coated nickel-rich ternary material has a flower-like structure. The preparation method of the present disclosure provides phosphate ions through the prepared phosphate solution, performs coating in a liquid phase environment, and synthesizes the precursor simultaneously by microwave hydrothermal synthesis, which is beneficial to the full contact between the phosphates and the precursor, and ensures the surface of the nickel-rich ternary precursor is uniformly coated with the phosphates. The method is simple and has good coating effect.

Abstract: Disclosed are a doped nickel-rich ternary material and a preparation method thereof. The preparation method comprises the following steps: (1) Mixing a nickel source, a cobalt source, and a manganese source in a solvent to obtain a solution A, adding oxidant and doping elements to the solution A, and stirring to obtain solution B; (2) Adding a complexing agent and nitric acid to the solution B and stirring to obtain solution C; (3) Drying the solution C to obtain aerogel D; (4) Grinding the aerogel D, and subjecting it to low-temperature pre-calcinating, and heating the aerogel to perform first calcinating to obtain precursor powder E; (5) Mixing the precursor powder E with a lithium source to obtain a mixture, and subjecting the mixture to second calcinating, grinding, and screening to obtain the doped nickel-rich ternary material.