Abstract: The invention provides a method for producing a heat insulating material composed of a hydrophobic aerogel, and the method includes the steps of: (1) mixing step; (2) hydrolysis step; (3) condensation step; (4) aging step; and (5) drying step. In the method, a siloxane compound, an inorganic gel, and a halogen-free surfactant are mixed and then a sol-gel process is performed to produce the aerogel heat-insulating material without water-washing. The produced heat-insulating material has preferable strength, smooth appearance, and low shrinkage and can overcome the powder-dropping problem. By the provided method, an aerogel heat-insulating board can be produced, or an aerogel cold-resisting and heat-insulating blanket can be produced by mixing with a fiber or a foam material.

Abstract: The invention provides a method for producing a heat insulating material composed of a hydrophobic aerogel, and the method includes the steps of: (1) mixing step; (2) hydrolysis step; (3) condensation step; (4) aging step; and (5) drying step. In the method, a siloxane compound, an inorganic gel, and a halogen-free surfactant are mixed and then a sol-gel process is performed to produce the aerogel heat-insulating material without water-washing. The produced heat-insulating material has preferable strength, smooth appearance, and low shrinkage and can overcome the powder-dropping problem. By the provided method, an aerogel heat-insulating board can be produced, or an aerogel cold-resisting and heat-insulating blanket can be produced by mixing with a fiber or a foam material.

Abstract: A method for producing a composite glue composed of an aerogel, an inorganic fiber, and an inorganic adhesive includes the following steps of: (1) mixing step, (2) hydrolysis step, (3) condensation step, (4) aging step, (5) high-temperature solvent replacement step, (6) evaporation and drying step, and (7) composition step. The obtained product thereof is a viscous composite glue composed of the aerogel, and the total content of the aerogel and an inorganic fiber is of 25-90 wt % after dried. Additionally, the obtained product can be used at a high temperature of more than 600° C., and has no phenomena of inorganic material decomposition and carcinogen production.