Abstract: A method for producing a black plated resin part includes the steps of electroplating a resin substrate provided with an underlying plating layer in a trivalent chromium plating bath containing thiocyanic acid, to thereby form, on the underlying plating layer, a black chromium plating layer composed of trivalent chromium and having a thickness of 0.15 ?m or more; and immersing the resin substrate provided with the black chromium plating layer in warm water at 30° C. or higher for a predetermined time. In the method, the amount of thiocyanic acid contained in the trivalent chromium plating bath, the temperature of the warm water, and the time of immersion of the resin substrate in the warm water are adjusted so that the black chromium plating layer exhibits a b* value of ?1.7 or less based on the L*a*b* color system.

Abstract: A black plated resin part includes a resin substrate, an underlying plating layer formed on the resin substrate, and a black chromium plating layer formed of trivalent chromium and having a thickness of 0.15 ?m or more. The black chromium plating layer is formed on the underlying plating layer. The chromium in the black chromium plating layer is present in the form of metallic chromium, chromium oxide, and chromium hydroxide, and the black chromium plating layer exhibits a b* value of 3.0 or less based on the L*a*b* color system.

Abstract: A method for producing a black plated resin part includes the steps of electroplating a resin substrate provided with an underlying plating layer in a trivalent chromium plating bath containing thiocyanic acid, to thereby form, on the underlying plating layer, a black chromium plating layer composed of trivalent chromium and having a thickness of 0.15 ?m or more; and immersing the resin substrate provided with the black chromium plating layer in warm water at 30° C. or higher for a predetermined time. In the method, the amount of thiocyanic acid contained in the trivalent chromium plating bath, the temperature of the warm water, and the time of immersion of the resin substrate in the warm water are adjusted so that the black chromium plating layer exhibits a b* value of ?1.7 or less based on the L*a*b* color system.

Abstract: A black plated resin part includes a resin substrate, an underlying plating layer formed on the resin substrate, and a black chromium plating layer formed of trivalent chromium and having a thickness of 0.15 ?m or more. The black chromium plating layer is formed on the underlying plating layer. The chromium in the black chromium plating layer is present in the form of metallic chromium, chromium oxide, and chromium hydroxide, and the black chromium plating layer exhibits a b* value of 3.0 or less based on the L*a*b* color system.