Abstract: Provided is a material having an excellent sound-absorbing performance which can be easily applied to the desired area at the operation site and which can effectively prevent sound leakage. The material includes an open-cell soft polyurethane foam prepared from a 2-part reactive urethane resin composition prepared from a polyisocyanate component and a polyol-containing component, wherein the polyol-containing component comprises a polyol component, catalysts, a foam stabilizer, an amine compound having primary or secondary amino groups, and carbon dioxide; wherein an average sound absorption coefficient of said polyurethane foam is 30% or more, measured in accordance with JIS A 1405-2:2007 for 63 hertz to 5000 hertz; and the length of liquid-dripping is within 300 mm.

Abstract: The present invention provides a composition which is capable of forming a polyurethane foam having a high hardness and excellent sound absorption properties. [Solution] The present invention relates to a composition for forming polyurethane foam characterized in that the composition for forming polyurethane foam comprises a polyol, a polyisocyanate, and a catalyst, in which the polyol comprises a polyol (A) having a number average molecular weight of 1500 to 8000 g/mol, the catalyst comprises a trimerization catalyst, in which the polyurethane foam has an air permeability of not less than 0.1 L/sec.

Abstract: Provided is a material having an excellent sound-absorbing performance which can be easily applied to the desired area at the operation site and which can effectively prevent sound leakage. The material includes an open-cell soft polyurethane foam prepared from a 2-part reactive urethane resin composition prepared from a polyisocyanate component and a polyol-containing component, wherein the polyol-containing component comprises a polyol component, catalysts, a foam stabilizer, an amine compound having primary or secondary amino groups, and carbon dioxide; wherein an average sound absorption coefficient of said polyurethane foam is 30% or more, measured in accordance with JIS A 1405-2:2007 for 63 hertz to 5000 hertz; and the length of liquid-dripping is within 300 mm.

Abstract: A pneumatic tire with a noise damper has a noise damper made of porous resin foam and arranged on a tread inner surface. The noise damper is formed by a single annular body extending continuously in a tire circumferential direction. The noise damper has a core density in a range of from 35 to 65 kg/m3 and an overall density in a range of from 50 to 105 kg/m3. A maximum height of the noise damper from the tread inner surface is in a range of from 12 to 30 mm.

Abstract: The present invention is to provide a composition which can easily form a polyurethane resin which exerts particularly excellent damping properties in an operating temperature range. A resin composition for damping materials, including a polyol-containing component (A) and a polyisocyanate (B) is provided. The polyol-containing component (A) contains a castor oil. When the composition is cured, the peak on its Tan ? curve is 0.7 or more and the temperature for the peak is in a range of ?10° C. to 100° C.

Abstract: Provided is a material having an excellent sound-absorbing performance which can be easily applied to the desired area at the operation site and which can effectively prevent sound leakage The material includes a 2-part reactive urethane resin composition prepared from a polyisocyanate component and a polyol-containing component, wherein the polyol-containing component comprises a polyol component (a), catalysts (b), a foam stabilizer (c), an amine compound having primary or secondary amino groups (d), and carbon dioxide (e). The 2-part reactive urethane resin composition, when cured, is an open-cell soft polyurethane foam, wherein the average sound absorption coefficient of said polyurethane foam is 30% or more, measured in accordance with JIS A 1405-2:2007 for 63 hertz to 5000 hertz.

Abstract: The present invention is to provide a composition which can easily form a polyurethane resin which exerts particularly excellent damping properties in an operating temperature range. A resin composition for damping materials, including a polyol-containing component (A) and a polyisocyanate (B) is provided. The polyol-containing component (A) contains a castor oil. When the composition is cured, the peak on its Tan ? curve is 0.7 or more and the temperature for the peak is in a range of ?10° C. to 100° C.

Abstract: Reduced aldehyde emissions during heated storage of a polyurethane resin are obtained by including at least one sulfurous compound selected from the group consisting of hydrogen sulfites and disulfites in the polyol component from which that polyurethane is produced. The amount of the sulfurous compound added is generally from 0.02 to 2.0 parts by weight for every 100 parts by weight of the polyol component.