Abstract: Provided is a vinyl chloride-based resin composition having superior weatherability. The vinyl chloride-based resin composition comprises, with respect to 100 parts by mass of a vinyl chloride-based resin, (a) 0.001 to 10 parts by mass of at least one hindered amine compound and (b) 0.001 to 10 parts by mass of at least one selected from the group consisting of metal perchlorates, etc.

Abstract: A compound water-sealing sealant comprising a non-water-swelling thermoplastic resin (A), preferably a vinyl chloride resin, and a water-swelling resin (C) obtained by kneading together 10 to 97% by weight of the non-water-swelling thermoplastic resin (A) and 3 to 90% by weight of a water-swelling material (B). The compound water-sealing sealant is molded by the conjoint extrusion molding of the non-water-swelling thermoplastic resin (A) and the water-swelling resin (C). The water-swelling material (B) is a water-swelling urethane resin which is a prepolymer having isocyanate groups in which the content of terminal NCO groups amounts to 1 to 12%, preferably 2 to 7%, obtained by the reaction of polyisocyanate with at least one polyether polyol of the formulaR[(OR.sub.1)n OH]pwherein R is a polyhydric alcohol residue;(OR.sub.

Abstract: A water-sealing sheet comprising a water-swelling resin obtained by kneading together 10 to 97% by weight of a non-water-swelling thermoplastic resin, preferably vinyl chloride resin, containing 80 to 200 parts by weight of a plasticizer based on 100 parts by weight of the non-waterswelling thermoplastic resin, and 3 to 90% by weight of a water-swelling urethane resin. The urethane resin is a prepolymer having isocyanate groups in which the content of terminal NCO groups amounts to 1 to 12%, preferably 2 to 7%, obtained by the reaction of polyisocyanate with at least one polyether polyol of the formulaR[(OR.sub.1)n OH]pwherein R is a polyhydric alcohol residue;(OR.sub.

Abstract: A halogenated resin composition whose heat stability, weatherability, initial coloration, thermal coloration and adhesiveness are improved by adding thereto an overbased alkaline earth metal carboxylate/carbonate complex together with a .beta.-diketone compound or a metal salt thereof.