Abstract: An electrode and a photoelectric semiconductor device using the same are provided. The electrode includes a pad layer, a barrier layer and a reflection layer, which are formed in order. The barrier layer is formed between the reflection layer and the pad layer.

Abstract: An apparatus for use in extracting milk from a human breast includes a pliant receiving member having an inner receiving portion sized to receive the human breast and an adjacent inner connecting portion defining an opening extending therethrough. The receiving member has an inner surface defining a recess located in the inner receiving portion and a passageway extending from the recess to the opening to provide fluid communication between the recess and the opening during use. The passageway provides fluid communication between the recess and the opening such that negative pressure can be generated between the recess and the breast.

Abstract: A packaging material used for a display device which is a desiccative-containing adhesive agent. The desiccative-containing adhesive agent is composed of a liquid-state organic material selected from a group including epoxy resin, polyurethane, bakelite, polyamide, acrylic resin and polysiloxane, and a solid-state desiccative selected from a group including alkaline metal oxide, alkaline-earth metal oxide, metallic halide, barium oxide, calcium oxide, calcium sulfate, calcium chloride, lithium chloride, calcium bromide, potassium Carbonate, aluminum oxide, magnesium oxide, copper sulfate, zinc chloride, zinc bromide, cobalt chloride, silica gel, zeolite and molecular sieve.

Abstract: A method for the preparation of a fiber reinforced modified phenolic resin composite, which comprises preparing a resole type phenolic resin having 60-75 wt % solid content and 5-10 wt % free aldehyde; preparing a blocked polyurethane resin having an average molecular weight of 2000-8000 and a viscosity of 500-1000 cps at 80.degree. C.; mixing the resole type phenolic resin, the blocked polyurethane resin and an acid catalyst at room temperature to form an impregnating resin, wherein the amount of the acid catalyst mixed is 2-10 wt %, based on the weight of the resole type phenolic resin, and the amount of the blocked polyurethane mixed is 5-20 wt %, based on the total weight of the mixed resins; and impregnating a plurality of filaments with the impregnating resin, and curing the impregnated filaments with a heat treatment to form a fiber reinforced modified phenolic resin composite.