Abstract: This disclosure relates to ethylene interpolymer compositions. Specifically, ethylene interpolymer products having: a Dilution Index (Yd) greater than 0; total catalytic metal ?3.0 ppm; ?0.03 terminal vinyl unsaturations per 100 carbon atoms, and; optionally a Dimensionless Modulus (Xd) greater than 0. The disclosed ethylene interpolymer products have a melt index from about 0.3 to about 500 dg/minute, a density from about 0.869 to about 0.975 g/cm3, a polydispersity (Mw/Mn) from about 2 to about 25 and a CDBI50 from about 20% to about 97%. Further, the ethylene interpolymer products are a blend of at least two ethylene interpolymers; where one ethylene interpolymer is produced with a single-site catalyst formulation and at least one ethylene interpolymer is produced with a heterogeneous catalyst formulation.

Abstract: This disclosure relates to ethylene interpolymer compositions and films prepared therefrom. Specifically: ethylene interpolymer products having: a dimensionless nonlinear rheology network parameter, ?int., greater than or equal to 0.01, satisfying 0.01×(Z?50)0.78??int.?0.01×(Z?60)0.78 inequality wherein Z is a normalized molecular weight defined by Z = M w M e where Mw and Me are the weight average and entanglement molecular weights, and; a residual catalytic metal of from ?0.03 to ?5 ppm of hafnium. The disclosed ethylene interpolymer products have a melt index from about 0.3 to about 500 dg/minute, a density from about 0.855 to about 0.975 g/cc, a polydispersity, M w M n , from about 1.7 to about 25 and a Composition Distribution Breadth Index (CDBI50) from about 1% to about 98%.

Abstract: This disclosure relates to ethylene interpolymer product having intermediate branching. Intermediate branching was defined as branching that was longer than the branch length due to comonomer and shorter than the entanglement molecular weight (Me). Intermediately branched ethylene interpolymer products were produced in a continuous solution polymerization process employing an intermediate branching catalyst formulation. Intermediately branched ethylene interpolymer products were characterized by a Non-Comonomer Index Distribution (NCIDi), a melt index from 0.3 to 500 dg/minute, a density from 0.858 to 0.965 g/cm3, a polydispersity (Mw/Mn) from about 2 to about 25 and a CDBI50 from about 10% to about 98%. A method based on triple detection cross fractionation chromatography (3D-CFC) was disclosed to measure NCIDi.

Abstract: This disclosure relates to ethylene interpolymer compositions. Specifically, ethylene interpolymer products having: a Dilution Index (Yd) greater than 0; total catalytic metal ?3.0 ppm; ?0.03 terminal vinyl unsaturations per 100 carbon atoms, and; optionally a Dimensionless Modulus (Xd) greater than 0. The disclosed ethylene interpolymer products have a melt index from about 0.3 to about 500 dg/minute, a density from about 0.869 to about 0.975 g/cm3, a polydispersity (Mw/Mn) from about 2 to about 25 and a CDBI50 from about 20% to about 97%. Further, the ethylene interpolymer products are a blend of at least two ethylene interpolymers; where one ethylene interpolymer is produced with a single-site catalyst formulation and at least one ethylene interpolymer is produced with a heterogeneous catalyst formulation.

Abstract: Embodiments of the invention described herein relate to a polyethylene polymer composition suitable for use in the manufacture of packaging articles, flexible films and/or sheets. In one embodiment, the copolymer comprises a polyethylene resin with density 0.918 g/cm3 to about 0.935 g/cm3, G? at G?(500 Pa) value, as determined from Dynamic Mechanical Analysis at 190° C., of less than 40 Pa, Mz/Mw of greater than 2, CDBI50 of greater than 60. Other embodiments relate to polymer compositions with defined molecular characteristics and formulations suitable for use in the manufacture of articles including films, sheets, bags and pouches with improved creep resistance and high toughness and a good balance of film stiffness and processability in monolayer and/or multi-layer film structures.

Abstract: Embodiments of the invention described herein relate to a polyethylene polymer composition suitable for use in the manufacture of packaging articles, flexible films and/or sheets. In one embodiment, the copolymer comprises a polyethylene resin with density 0.918 g/cm3 to about 0.935 g/cm3, G? at G?(500 Pa) value, as determined from Dynamic Mechanical Analysis at 190° C., of less than 40 Pa, Mz/Mw of greater than 2, CDBI50 of greater than 60. Other embodiments relate to polymer compositions with defined molecular characteristics and formulations suitable for use in the manufacture of articles including films, sheets, bags and pouches with improved creep resistance and high toughness and a good balance of film stiffness and processability in monolayer and/or multi-layer film structures.

Abstract: Embodiments of the invention described herein relate to a polyethylene polymer composition suitable for use in the manufacture of packaging articles, flexible films and/or sheets. In one embodiment, the copolymer comprises a polyethylene resin with density 0.918 g/cm3 to about 0.935 g/cm3, G? at G?(500 Pa) value, as determined from Dynamic Mechanical Analysis at 190° C., of less than 40 Pa, Mz/Mw of greater than 2, CDBI50 of greater than 60. Other embodiments relate to polymer compositions with defined molecular characteristics and formulations suitable for use in the manufacture of articles including films, sheets, bags and pouches with improved creep resistance and high toughness and a good balance of film stiffness and processability in monolayer and/or multi-layer film structures.

Abstract: The productivity of a catalyst in a gas phase polymerization of olefins (e.g. grams of polymer per gram of catalyst) may be increased by including in the gas phase from 1 to 20 weight % of an inert non-polymerizable hydrocarbon. The hydrocarbon may be in gaseous form but preferably is in liquid form.

Abstract: Electronic packaging films, tapes, bags and pouches having excellent optical properties and heat sealability, low hexane extractables and a good balance of physical properties may be prepared from linear low density polyethylene having a melt flow ratio (I21/I2) from about 23 to about 32, prepared in a tandem dual reactor solution phase polymerization in the presence of a phosphinimine catalyst and a co-catalyst system which comprises an aluminum based co-catalyst, an ionic activator or a mixture thereof.

Abstract: Food packaging films, bags and pouches having excellent optical properties and heat sealability, low hexane extractables and a good balance of physical properties may be prepared from linear low density polyethylene having a melt flow ratio (I21/I2) from about 23 to about 32, prepared in a tandem dual reactor solution phase polymerization in the presence of a phosphinimine catalyst and a co-catalyst system which comprises an aluminum based co-catalyst, an ionic activator or a mixture thereof.

Abstract: Medical packaging films, bags and pouches having excellent optical properties and heat sealability, low hexane extractables and a good balance of physical properties may be prepared from linear low density polyethylene having a melt flow ratio (I21/I2) from about 23 to about 32, prepared in a tandem dual reactor solution phase polymerization in the presence of a phosphinimine catalyst and a co-catalyst system which comprises an aluminum based co-catalyst, an ionic activator or a mixture thereof.

Abstract: Bags, other than food contact or medical bags, having a good balance of properties may be prepared from linear low density polyethylene having a melt flow ratio (I21/I2) from about 23 to about 32, prepared in a tandem dual reactor solution phase polymerization in the presence of a phosphinimine catalyst and an aluminum based activator in the first reactor and an ionic activator in the second reactor.

Abstract: The present invention provides a novel process for preparing a catalyst useful in gas phase polymerization of olefins wherein the physical properties of the polymer and the productivity of the catalyst can be altered depending on the sequence of addition of the catalyst components. The catalyst consists of compounds of Ti, Mg, Al and optionally an electron donor supported on an amorphous support.