Abstract: Provided is a galvanized steel sheet having a TS of 980 MPa or more, high YS, excellent ductility, strain hardenability, and hole expansion formability. A base steel sheet has a defined chemical composition and a steel microstructure as follows: area ratio of ferrite: 65.0% or less (including 0%), area ratio of bainitic ferrite: 5.0% or more and 40.0% or less, area ratio of tempered martensite: 0.5% or more and 80.0% or less, area ratio of retained austenite: 3.0% or more, area ratio of fresh martensite: 20.0% or less (including 0%), SBF+STM+2×SMA: 65.0% or more, SMA1/SMA: 0.80 or less, and SMA2/SMA: 0.20 or more.

Abstract: To provide at least one of: a powder composition from which a calcined body with similar processability can be produced without requiring the application of different forming conditions and calcination conditions for each composition; a method for producing the powder composition; a calcined body produced from the powder composition; a method for producing the calcined body; and uses thereof. A powder composition including: two or more types of zirconia in which a lanthanoid rare-earth element is dissolved; a transition metal element other than zirconium and hafnium; and a remainder composed of zirconia stabilized only by one or more selected from the group consisting of yttrium, calcium and magnesium, wherein a different lanthanoid rare-earth element is dissolved in each zirconia in which the lanthanoid rare-earth element is dissolved, and a transition metal element content is 1500 ppm or less.