Abstract: A method for manufacturing an austenitic stainless steel strip comprises: hot-rolling a material having a component composition containing, in % by mass, more than 20.0% and 30.0% or less of Ni, more than 15.0% and 18.0% or less of Cr, 1.0 to 2.0% of Mo, 3.5% or more and less than 5.0% of Al, more than 1.0% and 2.0% or less of Nb+Ta, 0.3% or less of Ti+V, 1.0% or less of Si, 2.0% or less of Mn, 0.01 to 0.3% of Zr, 0.005 to 0.045% of C, 0.001 to 0.03% of B, and also containing at least one element selected from Y, La, Ce and Hf in an amount such that the content of Y+La+Ce+Hf+Zr can become 0.01 to 0.5% with the remainder comprising Fe and unavoidable impurities; cold-rolling the strip; and heating the strip, then maintaining the strip at that temperature, and rapid-cooling the strip.

Abstract: The present invention provides a Ni-based alloy that is hot-workable and exhibits an excellent high-temperature strength, and provides a heat-resistant plate material using the same. This Ni-based alloy is composed of, by mass, C: 0.002 to 0.10%, Si: less than 1.0%, Mn: up to 1.0%, P: up to 0.04% (including 0%), S: up to 0.01% (including 0%), Cr: 15.0 to 25.0%, Co: 0.1 to 18.0%, Mo: not less than 2.0% and less than 4.0%, Al: 3.0 to 5.0%, Ti: not less than 0.01% and less than 0.5%, Zr: 0.01 to 0.1%, B: 0.001 to 0.015%, Fe: up to 3.0%, Mg or Mg+0.6×Ca: 0.0005 to 0.01%, N: up to 0.01% (including 0%), O: up to 0.005% (including 0%), and the balance of Ni with inevitable impurities, S/Mg or S/(Mg+0.6×Ca) being up to 1.0, and a G value represented by the following formula (1) being 30 to 45. G=7+0.11Cr+8.23Al+4.66Ti?0.

Abstract: The present invention provides a Ni-based alloy that is hot-workable and exhibits an excellent high-temperature strength, and provides a heat-resistant plate material using the same. This Ni-based alloy is composed of, by mass, C: 0.002 to 0.10%, Si: less than 1.0%, Mn: up to 1.0%, P: up to 0.04% (including 0%), S: up to 0.01% (including 0%), Cr: 15.0 to 25.0%, Co: 0.1 to 18.0%, Mo: not less than 2.0% and less than 4.0%, Al: 3.0 to 5.0%, Ti: not less than 0.01% and less than 0.5%, Zr: 0.01 to 0.1%, B: 0.001 to 0.015%, Fe: up to 3.0%, Mg or Mg+0.6×Ca: 0.0005 to 0.01%, N: up to 0.01% (including 0%), O: up to 0.005% (including 0%), and the balance of Ni with inevitable impurities, S/Mg or S/(Mg+0.6×Ca) being up to 1.0, and a G value represented by the following formula (1) being 30 to 45. G=7+0.11Cr+8.23Al+4.66Ti-0.