Abstract: A process including an apparatus for use therein for gasifying a carbonaceous material by means of blowing said carbonaceous material onto a high temperature molten iron bath through a top-blowing lance of the non-immersion type is disclosed.

Abstract: Herein is disclosed a process for producing an alloy of low phosphorus content by means of a furnace equipped with a lance for injection. The process is characterized by producing an alloy of low phosphorus content and at the same time by gasifying the carbonaceous material.The process comprises the steps of:forming a bath of molten metal by pouring a molten metal in the furnace, said molten metal containing not more than 0.040% of phosphorus;injecting by means of said lance into said bath of molten metal a carbonaceous material together with a gasifying agent to gasify the carbonaceous material with the heat of the bath of molten metal and to increase the carbon content of the bath of molten metal, said carbonaceous material containing not more than 0.035% of phosphorus;adding to said bath of molten metal an alloying element to react with the molten metal thereby forming an alloy; andrecovering the formed gas and, at the same time, obtaining the alloy of low phosphorus content.

Abstract: A process for producing an ultra-low phosphorus steel containing 0.010% or less of phosphorus is disclosed, which comprises charging a desiliconized pig iron into a top- and bottom-blowing oxygen converter, introducing a slag-forming agent in a powdered form onto the molten iron together with the top-blowing oxygen and introducing a bottom-blowing gas selected from the group consisting of an inert gas, nitrogen gas, oxygen gas, carbon monoxide gas, carbon dioxide gas and mixtures thereof during the oxygen top-blowing or during both the oxygen top-blowing and the subsequent tapping.

Abstract: In a process for the gasification of solid carbonaceous material such as coal, powdered coal is top-blown onto a molten iron bath stored in a furnace through a non-submerged lance toward a hot spot formed by means of a jet of oxygen and steam top-blown through a non-submerged lance, coal being blown by means of a carrier gas, and flux is optionally added into the furnace by the lump or blown toward the hot spot, thereby the coal being gasified. The ratio L/L.sub.o of the depression depth L of the molten iron bath to the molten iron bath depth L.sub.o is maintained from 0.05 to 0.15, and the blowing velocity of the solid carbonaceous material is maintained from 50 to 300 m/sec so as to suppress the forming of an adhered mass in the furnace. A stirring gas is blown through a bottom nozzle to stir the molten iron bath.