Abstract: A ceramics sintered body improved in corrosion resistance to a molten metal and a method for producing such a ceramics sintered body. The ceramics sintered body includes boron nitride, titanium diboride, a calcium compound and titanium nitride and having a relative density of 92% or more, wherein the content of the calcium compound in terms of CaO is from 0.05 to 0.8% by weight, and a peak intensity by X-ray diffraction of the (200) plane derived from titanium nitride is from 0.06 to 0.15 relative to a peak intensity of the (002) plane of BN. Further, a method for producing a ceramics sintered body, which is applicable to the ceramics sintered body, and an exothermic body for metal vapor deposition constituted by the ceramics sintered body are also disclosed.

Abstract: A metal evaporation boat having improved wettability to a molten metal and having a prolonged life, and a method for evaporating a metal employing it. A metal evaporation heating element characterized by having one or more grooves in a direction not in parallel with a current direction, on an upper surface of a ceramic sintered body comprising titanium diboride (TiB2) and/or zirconium diboride (ZrB2), and boron nitride (BN). It is preferred that the direction not in parallel with the current collection is from 20 to 160° C. to the current direction, that the ceramic sintered body has a cavity and the groove is formed on the bottom surface thereof, and that a predetermined pattern is drawn by a plurality of grooves on the upper surface of the ceramic sintered body and/or on the upper surface of the cavity.

Abstract: A ceramics sintered body improved in corrosion resistance to a molten metal and a method for producing such a ceramics sintered body. The ceramics sintered body includes boron nitride, titanium diboride, a calcium compound and titanium nitride and having a relative density of 92% or more, wherein the content of the calcium compound in terms of CaO is from 0.05 to 0.8% by weight, and a peak intensity by X-ray diffraction of the (200) plane derived from titanium nitride is from 0.06 to 0.15 relative to a peak intensity of the (002) plane of BN. Further, a method for producing a ceramics sintered body, which is applicable to the ceramics sintered body, and an exothermic body for metal vapor deposition constituted by the ceramics sintered body are also disclosed.